Previous issue date: 2016-07-07 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / A liga AA 356 é uma liga Al-Si amplamente utilizada tanto na indústria automobilística como na aeronáutica. Para melhorar suas propriedades mecânicas, são usados inoculantes para o refino de grão e para modificação eutética. Os componentes solidificados em moldes metálicos, que são mais eficientes na extração de calor, em geral, têm propriedades mecânicas superiores àqueles solidificados em moldes de areia que apresentam uma menor taxa de extração de calor. A curva de resfriamento que é uma curva da temperatura em função do tempo obtida da extremidade de um termopar localizado no centro do molde e conectado a um sistema de aquisição de dados é uma ferramenta que permite avaliar tanto o refino de grão quanto a modificação eutética. Essa ferramenta permite observar também a formação de fases intermetálicas, e é influenciada por fatores como a taxa de resfriamento. A primeira derivada da curva de resfriamento que representa a taxa de resfriamento é parte da ferramenta, pois melhora a precisão dos dados obtidos com a curva de resfriamento. Para o desenvolvimento desse trabalho foram preparados lingotes variando-se o material do molde (areia e aço), o teor de modificador de eutético e a adição de refinador de grão, ambos na forma de ligas-mãe (ante-liga) Al-10Sr e Al-5Ti-1B, respectivamente. Os valores para traçar as curvas de resfriamento foram obtidos monitorando a temperatura do metal desde o vazamento até sua completa solidificação e posterior resfriamento. Amostras do material foram preparadas para metalografia e obtidas imagens de macroestrutura e microestrutura. Da microestrutura foram obtidas as imagens com o ataque químico convencional e o ataque químico profundo; foram realizadas medidas de fração de porosidade por área, por técnica de microscopia, além de medidas de dureza Vickers e Brinell. Os resultados confirmam que a técnica da análise térmica da curva de resfriamento é uma excelente ferramenta, pois além de fornecer as temperaturas solidus e liquidus, as temperaturas de transformações de fases e informações sobre a eficácia do refino de grão e modificação eutética, pode ser utilizada na avaliação da presença de impurezas e na identificação de fases presentes nas ligas, tanto da liga primária quanto da liga reciclada. / The alloy AA 356 is an Al-Si alloy widely used in the automotive and aeronautics industry. To improve the mechanical properties of this alloy inoculants are used to grain refine and eutectic modification. The solidified components in metal mold, with a higher heat extraction rate, generally have mechanical properties superior to those solidified in sand mold with a lower heat extraction rate. The cooling curve is a curve of temperature versus time obtained in the end of a thermocouple located in the center of the mold and connected to a data acquisition system. It is a tool to evaluate both the grain refinement as the eutectic modification. This tool also can also be used to observe the formation of intermetallic phases, and is influenced by factors such as the cooling rate. The first derivative of the curve representing the cooling rate is part of the tool because it improves the accuracy of the data obtained from the curve. For the development of this work ingots were prepared varying the mold material (sand and steel), the content of eutectic modifier and the grain refiner addition , both in the form of master alloys Al-10Sr and Al-5Ti-1B, respectively.The data for plotting the cooling curves were obtained experimentally during solidification; Samples of the material were prepared for metallography and macrostructure and microstructure images were obtained. Through microstructure images obtained with conventional etching and deep etching. Porosity fraction area was measured by microscopy technique and hardness measurements were performed by Vickers and Brinell metdhod. The results confirm that the thermal analysis of the cooling curve is an excellent tool because provides the solidus and liquidus temperatures and the phase transformations on the effectiveness of the grain refining and eutectic modification and it can be used to assess the presence of impurities in the phase identification, for both the primary alloy and the recycled alloy.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/141999 |
| Date | 07 July 2016 |
| Creators | Silva, Cássia Cavalcanti [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Kiyan, Carlos [UNESP], Simões, Alexandre Zirpoli [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 600 |
Page generated in 0.0027 seconds