The relationship between crack path and test method was examined by comparing the performance of adhesive-adherend combinations (six) in quasi-static fracture, mixed-mode fatigue, and creep crack growth. Crack paths in creep and quasi-static fracture were similar due to similar crack-tip plastic zone sizes in the epoxy adhesive even though the crack growth rates in creep were much smaller. Under condensed moisture and mixed-mode, creep and threshold fatigue tests produced interfacial failure. Under room-temperature dry environment, near threshold mixed-mode fatigue was interfacial, but was not in creep or quasi-static fracture. Smaller plastic zone size and crack path proximity to the interface that followed increased the sensitivity of near threshold, mixed-mode fatigue to surface properties. Therefore, the interfacial or cohesive failure of an adhesive system, which may judge the quality of the bond, can be a function of the test being conducted and may not be an absolute indicator of joint quality.
| Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:OTU.1807/33256 |
| Date | 20 November 2012 |
| Creators | Jhin, Minseok |
| Contributors | Spelt, Jan K., Papini, Marcello |
| Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
| Language | en_ca |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0019 seconds