Ti-6Al-4V, known for high strength-to-weight ratio and good resistance to corrosion, has been widely used in aerospace, biomedical, and high-performance sports applications. A wide range of physical and mechanical properties of Ti-6Al-4V can be achieved by varying the microstructures via deformation and recrystallization processes. The aim of this thesis is to establish a microstructure-sensitive fatigue analysis approach that can be applied in engineering applications such as fretting fatigue to permit explicit assessment of the influence of microstructure. In this thesis, crystal plasticity constitutive relations are developed to model the cyclic deformation -TiAl has beenabehavior of Ti-6Al-4V. The development of the slip bands within widely reported and has been found to play an important role in deformation and fatigue behaviors of Ti-6Al-4V. The shear enhanced model is used to simulate the formation and evolution of slip bands triggered by planar slip under static or quasi-static loading at room temperature. Fatigue Indicator Parameters (FIPs) are introduced to reflect driving force for the different crack formation mechanisms in Ti-6Al-4V. The cyclic stress-strain behavior and fretting fatigue sensitivity to microstructure and loading parameters in dual phase Ti-6Al-4V are investigated.
| Identifer | oai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/22669 |
| Date | 10 March 2008 |
| Creators | Zhang, Ming |
| Publisher | Georgia Institute of Technology |
| Source Sets | Georgia Tech Electronic Thesis and Dissertation Archive |
| Detected Language | English |
| Type | Dissertation |
Page generated in 0.002 seconds