Five series of PT-30/organoclay (Cloisite 10A, Cloisite 30B, Nanomer I.28E, Nanomer I.30E and Nanomer I.44PA) composites were prepared and characterized. The dispersion of clay tactoids in PT-30 resin was studied by XRD and TEM. XRD analyses determined that the d-spacings of each nanoclays of these were expanded upon dispersing in the PT-30 matrix versus the as-received clay. TEM micrographs further demonstrated that the intercalation of clay layers by PT-30 occurred during the curing process. Histograms of clay tactoids distributions were generated based on the combination of XRD and TEM results. The glass transition temperatures (Tg) of selected PT-30/clay composites were measured by DSC and compared. Partial clay exfoliation with some resin intercalation was demonstrated. The average flexural strengths and flexural moduli of all composites were obtained using three-point bending tests.
| Identifer | oai:union.ndltd.org:MSSTATE/oai:scholarsjunction.msstate.edu:td-1996 |
| Date | 05 August 2006 |
| Creators | Huang, Gang |
| Publisher | Scholars Junction |
| Source Sets | Mississippi State University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses and Dissertations |
Page generated in 0.0018 seconds