Orientador: Wilkens Aurelio Buarque e Silva / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-24T18:40:10Z (GMT). No. of bitstreams: 1
Lameira_DeborahPacheco_D.pdf: 11244410 bytes, checksum: 54506eb4da406d4e27116632cc014de5 (MD5)
Previous issue date: 2014 / Resumo: O objetivo deste estudo foi avaliar a resistência à fratura de coroas monolíticas e bicamada a base de zircônia, após envelhecimento artificial. Para este estudo, foram utilizados 32 incisivos bovinos onde foram feitos preparos de coroa total. Estes foram escaneados para a confecção de coroas a base de a zircônia tetragonal parcialmente estabilizada por ítrio (yttrium partially stabilized tetragonal zirconia polycrystalline Y-TZP), por um sistema CAD/CAM (computer-aided design and computer-aided manufacturing). As coroas foram fabricadas de acordo com os grupos experimentais (n=10/grupo): Coroa monolítica de zircônia polida PM (1.5mm de espessura); Coroa monolítica de zircônia com aplicação de glaze GM (1.5mm de espessura); Coroa bicamada com coping de zircônia BL (0.8mm de espessura) com cerâmica de cobertura (0.7mm de espessura). As coroas foram cimentadas nos respectivos preparos com cimento resinoso (RelyX Unicem-2, 3M-ESPE). Após a cimentação, as amostras foram submetidas ao envelhecimento artificial em uma simuladora de mastigação (2,5 milhões de ciclos/3Hz de frequência/8kg) em saliva artificial a 37°C, em seguida foi efetuado o teste de resistência à fratura em maquina Instron, com velocidade de 0,5 mm/min. Duas coroas remanescentes referente a PM e GM foram submetidas a análise estrutural Electron probe microanalysis (EPMA), para medir o nível de ítrio após o envelhecimento. Os resultados foram submetidos a Análise de Variância e teste de Tukey (p=0.05). O modo de fratura foi avaliado por meio de Microscopia Eletrônica de Varredura (MEV). As coroas de zircônia monolíticas apresentaram resultados semelhantes de resistência à fratura (PM = 3476,2N ± 791,7; GM = 3561,5N ± 991,6), que foram maiores (p=0,02) do que os resultados para as coroas bicamada (BL = 2060,4N ± 810,6). Não houve diferença significativa na quantidade de ítrio entre as superfícies oclusais desgastas (PM, GM), e na superfície não desgastada de PM. Destes modo, a resistência à fratura de coroas monolíticas foi maior do que de coroas na configuração bicamada / Abstract: The purpose of this study was to evaluate the fracture strength and failure mode of zirconia crowns in monolithic or bi-layer configuration after artificial aging. Thirty-two bovine incisors received crown preparation and were scanned for the manufacturing of Y-TZP crowns using CAD/CAM technique. Crowns were fabricated according to the following groups (n=10/group): PM polished monolithic zirconia crowns of 1.5mm uniform thickness; GM glazed monolithic zirconia crowns of 1.5mm uniform thickness; BL bi-layer crowns with 0.8mm zirconia core and 0.7mm of veneered porcelain. All crowns were cemented on each respective tooth with resin cement (RelyX Unicem-2, 3M-ESPE). After the cementation, specimens were submitted to artificial aging in a chewing simulator (2.5 million cycles/ 3Hz frequency/8kg) in artificial saliva at 37°C, then the samples were submitted to fracture strength test (Instron) at a crosshead speed of 0.5mm/min. Two remaining crowns referring to PM and GM were submitted to Electron probe microanalysis (EPMA), to measure the yttrium levels after aging. One-way ANOVA and Tukey¿s test (p=0.05) were employed for analysis of the results. The fracture mode was evaluated with Scanning Electron Microscope (SEM). Monolithic zirconia crowns presented similar fracture strength results (PM= 3476.2N ± 791.7; GM= 3561.5N ± 991.6), which were higher (p=0.02) than the results for the bi-layer crowns (BL= 2060.4N ± 810.6). There was no significant difference in the yttrium content among worn occlusal surfaces (PM, GM) and undamaged surface in PM. Thus, the fracture strength of monolithic zirconia crowns was higher than bi-layer configuration / Doutorado / Protese Dental / Doutora em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290241 |
| Date | 24 August 2018 |
| Creators | Lameira, Deborah Pacheco, 1982- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Silva, Wilkens Aurelio Buarque e, 1967-, Landulpho, Alexandre Brait, Paixão, Fernanda, Sinhoreti, Mário Alexandre Coelho, Branco, Filipe Polesi |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 36 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds