Previous issue date: 2001 / Resumo: O objetivo deste estudo foi avaliar a resistência à tração de discos de Titânio comercialmente puro unidos às resinas compostas de ativação química e física para fixação Panavia Fluoro Cement e Rely X ARC. Para a realização do experimento, 120 discos de Titânio foram fundidos, embutidos em tubos de PVC com resina acrílica autopolimerizável, planificados e polidos com lixas d'água de granulações 320, 400 e 600. Uma área circular central com 4mm de diâmetro da superfície dos discos de Titânio foi submetida ao jateamento com óxido de Alumínio (50 mm) e os discos limpos em água sob ultra-som por 10 minutos. Os espécimes foram divididos em 4 Grupos de 30 cada. Nos Grupos 1 e 3 os discos foram unidos aos 10 minutos após o jateamento e os Grupos 2 e 4 vinte e quatro horas após o jateamento. Nos Grupos 1 e 2 os discos de Titânio foram unidos com a resina composta Panavia Fluoro Cement, e os Grupos 3 e 4 com a resina composta Rely X ARe. Após armazenagem em água destilada a 37°C por 24 horas, os corpos-de-prova foram submetidos a ensaio de tração axial em máquina de ensaio universal com velocidade de 0,5 mm/min. Os valores obtidos foram submetidos à análise de variância em nível de significância de 5%. As médias e os desvios padrões dos valores obtidos em MPa foram: Grupo 1: 13,96 (3,60); Grupo 2: 14,76 (7,71); Grupo 3: 13,90 (6,08) e Grupo 4: 18,27 (7,34). Não houve diferença estatística significante entre os grupos testados. A superfície dos corpos-de-prova fraturados foi observada em lupa estereoscópica com aumento de 60 vezes (60X) para a determinação do tipo de fratura provocada pelo ensaio de tração. Um corpo-de-prova de cada Grupo foi selecionado para observação em microscópio eletrônico de varredura. Ocorreu a combinação de falha adesiva entre resina composta e Titânio e coesiva da resina composta para fixação em todos os corpos-de-prova. Porém, nos Grupos I e 2 a falha predominante foi coesiva na resina composta para fixação Panavia Fluoro Cement e nos Grupos 3 e 4 a falha predominante foi adesiva entre a resina composta para fixação Rely X ARC e o Titânio / Abstract: The aim of this study was to evaluate the tensile bond strength of commercially pure Titanium bonded to the luting composite resins Panavia Fluoro Cement and Re1y X ARC. One hundred twenty Titanium discs were casted and embedded in PVC tubes with cold-cured acrylic resin. The edges of the Titanium discs containing tubes were cut and the Titanium discs were grounded on 320, 400 and 600 silicon carbide papers. Then, a 4mm diameter circular area was sandblasted (50 mm Aluminum oxide) and the specimens were ultrasonic cleaned for 10 minutes. The specimens were divided in four Groups with 30 specimens each. In the Groups 1 and 3 the discs were bonded in pairs at ten minutes and in the Groups 2 and 4 twenty-four hours after the sandblasting. The specimens of the Groups 1 and 2 were bonded with Panavia Fluoro Cement and the Groups 3 and 4 with the Rely X are. After the twenty-four hours storage in 37°C water, the bonded paired discs were submitted to the tensile test in a 0,5 mm/minute crosshead speed Instron Universal Machine. The tensile strength values were submitted to the analysis of variance (p=0,05). The means and standard deviations were: Group 1 - 13,96 (3,6); Group 2 - 14,76 (7,71); Group 3 - 13,90 (6,08); Group 4: 18, 27 (7,34). The higher tensile strength value was reached in the Group 4 and the smaller in the Group 3, but there was not statistically significant difference among the alI Groups. The surface of the fractured specimens was observed in a 60 x stereoscopic loupe to determinate the fracture shape. One specimen of each Group was selected to observation in scanning electronic microscopy. The fracture shape in the all Groups was a mixture of cohesive in the composite resin and adhesive failures. However, the predominant failure in the Groups 1 and 2 was cohesive in the composite resin and in the Groups 3 and 4 the predominant failure was adhesive between
the composite resin and Titanium / Mestrado / Mestre em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288186 |
| Date | 02 September 2001 |
| Creators | Schneider, Rafael |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Goes, Mario Fernando de, 1954-, Bottin, Marco Antonio, Martins, Luís Roberto Marcondes |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 90p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds