Previous issue date: 2017-05-02 / Sem bolsa / Este estudo avaliou a biocompatibilidade de diferentes materiais obturadores de canais radiculares de dentes decíduos e o seu potencial de alteração de cor. Foram avaliados os seguintes materiais: um material à base de MTA, um material à base de hidróxido de cálcio e iodofórmio (Vitapex), Óxido de zinco e eugenol (OZE), e um material à base de hidróxio de cálcio (Calen) espessado com óxido de zinco (ZO). Para a avaliação da biocompatibilidade, os materiais foram inseridos em tubos de polietileno e implantados no tecido subcutâneo dorsal de quinze ratos Wistar (Rattus norvegicus). Após 15, 30 e 60 dias, os animais foram eutanasiados, os tubos e tecidos circundantes foram removidos e histologicamente processados. As amostras foram avaliadas quanto à intensidade da resposta inflamatória, a espessura da cápsula fibrosa, presença de calcificação e células gigantes. Para a análise do potencial de discoloração, setenta e cinco blocos cubóides de esmalte-dentina foram preenchidos com os diferentes materiais obturadores e selados com ionômero de vidro fotoativado. A alteração de cor (?E00) foi calculada baseada nas coordenadas de cor medido com o espectrofotômetro (VITA Easyshadecompact) antes e depois da inserção dos materiais e após 1 semana, 1, 3, 6 e 9 meses. A alteração de cor ?E00 foi calculada pelo CIEDE 2000 para cada espécime a partir do baseline. Os resultados do teste de biocompatibilidade mostraram que os materiais apresentaram decréscimo na severidade da inflamação a partir de 30 dias. Da mesma forma, em todos os grupos, a cápsula fibrosa, inicialmente espessa, se tornou mais delgada ao longo do período experimental. Células gigantes foram observadas em todos os grupos experimentais principalmente no período de 15 dias, enquanto a ocorrência de calcificação foi observada com mais frequência no grupo Calen+ZO. O teste de avaliação da capacidade de indução de alteração de cor revelou que o tempo teve efeito nos valores de ?E00 (p <0,0001), assim como os materiais (p = 0,004). As interações entre tempo e os materiais provocaram alterações de (?E00) (p < 0,0001). O material à base de MTA apresentou menores valores de alteração de cor (?E= 3,02) ao longo do tempo enquanto o óxido de zinco e eugenol demonstrou os maiores valores (?E= 5,42) (p= 0,018). O material à base de MTA apresenta propriedades satisfatórias podendo ser uma alternativa aos materiais obturadores convencionais, para utilização em canais radiculares de dentes decíduos. / The aim of this study was to evaluate the biocompatibility and discoloration potential of experimental MTA-based endodontic filling material in comparison to zinc oxide eugenol (ZOE) cement, Calen paste thickened with zinc oxide, and Vitapex. In the biocompatibility assay, the materials were introduced into polyethylene tubes and implanted into the dorsal subcutaneous tissue of fifteen Wistar rats (Rattus norvegicus). After 15, 30 and 60 days, the animals were euthanized, the surrounding tubes and tissues were removed and processed for histopathological evaluation. The samples were analyzed for the intensity of the inflammatory response, the thickness of the fibrous capsule, presence of calcification and giant cells. For the analysis of discoloration potential, seventy-five cuboidal enamel-dentin blocks were filled with different endodontic filling materials and sealed with photoactivated glass ionomer cement. Standardized color measurements were performed using a spectrophotometer (Vita Easyshade, Vita-Zahnfabrik, Oberding, Germany) and expressed in ?E*00 units at the following intervals: prior to and after placement of the filling and after 1 week,1 month, 3 months, 6 months, and 9 months. The results of biocompatibility showed the materials tested, as well as the control, had a lower inflammation severity in 30 and 60 days in relation to 15 days. Likewise, the thickness of fibrous capsule in all groups of materials in 15 days was thick and decreased over time. It was possible to observe the presence of giant cells in all groups, mainly in 15 days. The presence of calcification was observed around implantation sites in all groups, but more frequently in Calen + ZO samples. The findings of discoloration potential exhibited the time had a significant effect on color variation values (?E*00) (p <0.0001).The effect of the materials on color variation (?E*00) was also statistically significant (p = 0.004). Interactions between time and materials demonstrated a significant effect on the values (?E*00) (p <0.0001). The MTA-based experimental material showed the smallest color variation throughout the experimental time (?E*00= 3.02), where as the zinc oxide and eugenol cement (ZOE) showed the highest darkening (?E*00= 5.42) (p = 0.018). ).In conclusion, experimental MTA-based material has satisfactory properties for use as endodontic filling material.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpel.edu.br:prefix/3641 |
| Date | 02 May 2017 |
| Creators | Pilownic , Katerine Jahnecke |
| Contributors | 93545037053, http://lattes.cnpq.br/1519551419752177, Romano, Ana Regina, Pappen, Fernanda Geraldo |
| Publisher | Universidade Federal de Pelotas, Programa de Pós-Graduação em Odontologia, UFPel, Brasil, Faculdade de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UFPEL, instname:Universidade Federal de Pelotas, instacron:UFPEL |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0032 seconds