Avaliação da adaptação interna, resistência de união e resistência à fratura da associação entre resinas bulk-fill e adesivos simplificados em dentes tratados endodonticamente /

Orientador: Milton Carlos Kuga / Resumo: O objetivo do presente estudo foi avaliar a adaptação interna (AI), resistência de união (RU) e resistência à fratura (RF) da associação entre resinas bulk-fill de alta viscosidade e adesivos simplificados, quando utilizados para restaurar dentes que foram endodonticamente tratados. Foram avaliados 4 sistemas restauradores comerciais, sendo eles Grupo Controle (GC): Scotchbond Multi-Purpose + Filtek Z350XT (3M/ESPE); (SBU/FBF) Single Bond Universal + Filtek Bulk-fill (3M/ESPE); (OBA/SF) OptBond All-in-one + Sonic Fill (Kerr) e (TBU/TBF)Tetric-N- Bond Universal + Tetric-N-Ceram Bulk-Fill (Ivoclar/Vivadent). Em 32 pré-molares humanos, a superfície oclusal foi planificada, cavidades classe I padronizadas foram confeccionadas e os dentes foram tratados endodonticamente .A irrigação foi feita com hipoclorito de sódio (NaOCl) 2,5% e EDTA 17%. Após a obturação (AH Plus, Dentsply, De Trey, Konstanz, Germany) e a limpeza da câmara pulpar com álcool 99%, foi aplicada uma fina camada de cimento de ionômero de vidro modificado por resina Ionoseal (VOCO, GmbH, Vuxhaven, Alemanha). Os dentes foram então divididos nos grupos experimentais (n=8), e as restaurações foram realizadas. Após 24 horas, os espécimes receberam um corte centralizado, as metades obtidas foram polidas e réplicas em resina epóxi para a avaliação da AI em microscopia eletrônica de varredura foram confeccionadas. Em 40 terceiros molares humanos, um corte foi feito para exposição da dentina profunda. Após a padronização da... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The objective of this study was to evaluate internal adaptation (IA), bond strength (BS), and fracture resistance (FR) of the combination of high-viscosity bulk-fill resins and simplified adhesives in the restoration of endodontically-treated teeth. Four commercial restoration systems were evaluated, which were the control group (CG) in which Scotchbond Multi-Purpose + Filtek Z350XT (3M/ESPE) was used, (SBU/FBF) Single Bond Universal + Filtek Bulk-fill (3M/ESPE); (OBA/SF) OptBond All-in-one + Sonic Fill (Kerr), and (TBU/TBF)Tetric-N- Bond Universal + Tetric-N-Ceram Bulk-Fill (Ivoclar/Vivadent). In 32 human pre-molars, the occlusal surface was flattened, standard class I cavities were created, and the teeth were treated endodontically. Irrigation was performed using 2.5% sodium hypochlorite (NaOCl) and 17% EDTA. After the fillings (AH Plus, Dentsply, De Trey, Konstanz, Germany) and cleaning of the pulp chamber with 99% ethanol, a thin layer of ionoseal resin-modified glass iomer luting cement was applied (Voco, GmbH, Vuxhaven, Germany). The teeth were then divided into the experimental groups (n=8) and the restorations were performed. After 24 hours, the specimens were sectioned in the middle and the halves obtained were polished, and replicas were made in epoxy resin to evaluate IA using scanning electron microscopy. In 40 human molar thirds, a cut was made to expose the deep dentin. After standardization of the smear layer (file # 600), the tissue was treated with 2.5% NaOCl... (Complete abstract click electronic access below) / Doutor

Identiferoai:union.ndltd.org:UNESP/oai:www.athena.biblioteca.unesp.br:UEP01-000915818
Date January 2019
CreatorsGirotto, Aline Carvalho
ContributorsUniversidade Estadual Paulista "Júlio de Mesquita Filho" Faculdade de Odontologia (Campus de Araraquara).
PublisherAraraquara,
Source SetsUniversidade Estadual Paulista
LanguagePortuguese
Detected LanguageEnglish
Typetext
Formatf.
RelationSistema requerido: Adobe Acrobat Reader

Page generated in 0.0017 seconds