Previous issue date: 2011-07-08 / O objetivo do presente estudo foi avaliar a resistência da união à microtração dos
sistemas adesivos convencional (Single Bond II, SB) e autocondicionante (Clearfil
SE Bond, SE) em dentina humana condicionada após a aplicação de agentes
dessensibilizantes. Foram utilizados discos obtidos de terceiros molares humanos
hígidos, os quais tiveram o esmalte oclusal removido para exposição de superfícies
planas de dentina média. Seis grupos foram formados, de acordo com os materiais
utilizados: G1 (controle) – hibridização com SB; G2 - dessensibilizante à base de
oxalato (BisBlock, BB) e SB; G3 - dessensibilizante à base de fluoreto (Aqua Prep F,
AF) e SB; G4 (controle) – hibridização com SE; G5 – BB e SE; G6 – AF e SE. Sobre
estas superfícies foram confeccionados blocos de resina composta Filtek Z350 de 5
mm de altura para obtenção de palitos de 1Ox1x1mm. Os corpos de prova foram
armazenados em água deionizada a 37° por 24h e submetidos ao ensaio mecânico
de microtração com velocidade de 1mm/min até a fratura. Os resultados foram
analisados através de ANOVA two-way e Teste Tukey (p<0,05). Os valores médios
dos grupos em MPa foram: G2 46,48 (8,04), G3 44,87 (11,26), G5 39,02 (13,45), G4
36,95 (7,14), G1 36,66 (10,84) e G6 32,71 (13,83) os quais não exibiram diferença
estatisticamente significativa entre si (p=0,012). Conclui-se que o uso combinado de
dessensibilizantes aos sistemas adesivos convencional e autocondicionante sobre a
dentina humana condicionada não alterou a resistência da união. / The aim of study was evaluate the microtensile bond strength of the total etch (Single
Bond II, SB) and self-etch adhesive systems (Clearfil SE Bond, SE) in human dentin
after desensitizer agents. Disks were obtained from human third molars, which had
their oclusal enamel removed to expose flat dentin surface. Six groups were formed
according to the materials used: G1 (control)- hybridization with SB, G2- oxalate
desensitizer (BisBlock, BB) and SB, G3- fluoride desensitizer (Aqua Prep F, AF) and
SB, G4 (control)- hybridization with SE, G5- BB and SE, G6- AF and SE. On these
surfaces were made blocks of composite Filtek Z350 of 5 mm to obtain “sticks”
10x1x1 mm. The specimens were stored in deionized water at 37°/ 24 h and
subjected to microtensile testing 1 mm/min until fracture. The images were observed
in MEV. The results were analyzed ANOVA two-way and Tukey test (p<0,05). The
mean values of the groups in MPa were: G2- 46.48(8.04), G3- 44.87(11.26), G5-
39.02 (13.45), G4-36.95(7.14), G1- 36.66(10.84) and G6- 32.71(13.83) which
showed no statistically significant difference between groups (p =0.012). It can be
concluded that the combined use the desensitizers and adhesive systems in human
dentin etched there is no influence on bond strength.
| Identifer | oai:union.ndltd.org:IBICT/oai:hermes.cpd.ufjf.br:ufjf/2054 |
| Date | 08 July 2011 |
| Creators | Teixeira, Vitória Celeste Fernandes |
| Contributors | Salvio, Luciana Andrea, Lopes, Murilo Baena, Leite, Fabíola Pessoa Pereira |
| Publisher | Universidade Federal de Juiz de Fora, Programa de Pós-graduação em Clínica Odontológica, UFJF, Brasil, Faculdade de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFJF, instname:Universidade Federal de Juiz de Fora, instacron:UFJF |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds