Previous issue date: 2015-02-23 / CNPq / A perfuração de poços de petróleo pode danificar fortemente a formação, incluindo a região de interesse: o reservatório. Perfurar sem que se danifique o reservatório caracteriza-se como um grande desafio, e por isso, tem sido estimulado o desenvolvimento de tecnologias de fluidos e otimização de processos de perfuração, incluindo, por exemplo, o uso de fluidos argilosos com vistas à minimização de perdas excessivas de filtrado para as formações permeáveis. Desta forma, este trabalho teve como objetivo avaliar a influência dos aditivos carboximetilcelulose (CMC) e calcita (CaCO3) e suas interações nas propriedades de filtração de fluidos de perfuração argilosos. Para tanto, foi utilizada uma amostra de argila bentonítica, comercialmente conhecida por Volclay, duas amostras de CMC com diferentes massas molares (CMC 1 (9,0 x 104g/mol) e CMC 2 (2,5 x 105g/mol)) e mesmo grau de substituição (DS = 0,7) e, duas amostras de calcita (CaCO3), com diferentes diâmetros médios de partículas e curvas de distribuição em tamanho. Foram realizadas a caracterização física e mineralógica da amostra de argila e a caracterização granulométrica das amostras de calcita, em seguida determinadas as propriedades reológicas (viscosidades aparente (VA) e plástica (VP), limite de escoamento (LE) e força gel (FG)) e de filtração (volume de filtrado (VF), volume de filtrado corrigido (VFcorr), spurt loss (SPL), espessura (h) e permeabilidade (k) do reboco e poder de retenção (R)) dos fluidos argilosos estudados. Os resultados evidenciaram que os fluidos estudados apresentaram comportamento pseudoplástico e os fluidos argilosos preparados com elevada concentração de CMC 2 (2g/350mL de água) apresentaram melhores valores
de propriedades reológicas, pois estas propriedades são fortemente influenciadas pelo grau médio de polimerização dos aditivos poliméricos. A aditivação de fluidos argilosos com carboximetilcelulose de baixa massa molar e com calcita de granulometria fina conferiu aos fluidos melhor desempenho na melhoria das propriedades de filtração. Isto aconteceu, porque no meio aquoso a CMC 1 em elevada concentração associada a calcita 1 conduziu a menores valores de VF, h e k e, elevados valores de R. / The drilling of oil wells can greatly damage the formation, including the region of interest: the reservoir. Drilling without damaging the reservoir is characterized as a big challenge, and therefore, has been stimulated the development of fluid technologies and optimization of drilling processes, including, for example, the clay fluids use aiming at minimization excessive losses of the filtrate into the permeable formations. Thus, this study aimed to evaluate the influence of additives carboxymethylcellulose (CMC) and calcite (CaCO3) and their interactions in the filtration properties of clay drilling fluids. For this, it was used a sample of bentonite clay, commercially known by Volclay, two samples of CMC with different molecular weight (CMC 1 (9,0 x 104g/mol) and CMC 2 (2,5 x 105g/mol) ) and the same degree of substitution (DS = 0,7) and two samples of calcite (CaCO3) with different average diameters of particles and size
distribution curves. It was done the physical and mineralogical characterization of the clay sample and the particle size characterization of the calcite samples it was also determined the rheological properties (apparent viscosity (AV) and plastic (PV), yield limit (YL) and gel strength (GS)) and of filtration (filtrate volume (FV), filtrate volume corrected (FVcorr), spurt loss (SPL), cake thickness (h) and permeability (k) and retaining power (R)) of the studied clay fluids. The results showed that the studied fluids showed pseudoplastic behavior and clay fluids prepared with high concentration of CMC 2 (2g/350mL of water) showed better values of rheological properties, because these properties are strongly influenced by the average degree of polymerization of polymeric additives. The additived clay fluids with low molecular weight carboxymethylcellulose and with fine granulometry calcite gave the fluids best performance in improving the
filtration properties. This happened because in the aqueous medium the CMC 1 in high concentration associated at calcite 1 led at lower values of FV, h and k and high values of R.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1058 |
| Date | 28 June 2018 |
| Creators | NÓBREGA, Karine Castro. |
| Contributors | AMORIM, Luciana Viana., LIRA , Hélio de Lucena., NOGUEIRA, Francisco Cézar Costa. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds