Luis Micahel - Dissertação.pdf: 3511320 bytes, checksum: a097f6e26c206ff84f45b15536bf9d80 (MD5) / O interesse em dispositivos limitadores de corrente supercondutores,
principalmente resistivos, tem aumentado significativamente nos últimos anos.
Dentre as principais características destes dispositivos, estão a capacidade de
limitação devido ao quenching do material, e o tempo de recuperação do estado
de supercondutividade. Várias configurações e materiais vêm sendo estudados
nos últimos anos, buscando melhorias na viabilidade construtiva deste tipo de
dispositivo. Este trabalho tem por objetivo o projeto e construção de um limitador
de corrente supercondutor resistivo (LCSR) modular, utilizando fitas
supercondutoras de alta temperatura de RE-Ba-Cu-O em paralelo, dispostas em
um enrolamento bifilar, sobre base de PLA (ácido polilático), ausente de
criostato. Foram realizadas medidas de curva V-I e também ensaios de curtocircuito
e de tempo de recuperação no material supercondutor, em criostato de
banho aberto, no LCSR modular imerso em nitrogênio líquido, a 77 K. Os
resultados apresentaram níveis de limitação e de recuperação promissores, e
viabilizaram a configuração e os materiais adotados. / The interest in superconducting current limiting devices, mainly resistive,
has increased significantly in recent years. Among the main characteristics of
these devices are the limiting capacity due to material quenching, and the
recovery time of the superconducting state. Several configurations and materials
have been studied in recent years, seeking improvements in the constructive
feasibility of this type of device. This work aims the design and construction of a
resistive-superconducting current limiter (RSCL) module, using RE-Ba-Cu-O high
temperature superconducting tapes connected in parallel, arranged in a bifilar
winding, on base made of PLA (polylactic acid), absent of cryostat. V-I curve
measures, short circuit and recovery time tests were performed in the modular
RSCL, which was immersed in an open bath cryostat with liquid nitrogen, at 77 K.
The results showed promising levels of limitation and recovery, making possible
the configuration and materials adopted.
| Identifer | oai:union.ndltd.org:IBICT/oai:https://app.uff.br/riuff:1/3937 |
| Date | 03 July 2017 |
| Creators | Rocha, Luís Micahel Martins |
| Contributors | Polasek, Alexander, Sass, Felipe, Martins, Helvio Jailson Azevedo, Sotelo, Guilherme Gonçalves, Dias, Daniel Henrique Nogueira |
| Publisher | Niterói |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFF, instname:Universidade Federal Fluminense, instacron:UFF |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds