Orientador: Gladis Camarini / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Civil, Arquitetura e Urbanismo / Made available in DSpace on 2018-08-19T14:19:57Z (GMT). No. of bitstreams: 1
Pereira_ValdirMoraes_M.pdf: 1471160 bytes, checksum: 1317b5951c4368324373d0e6c2a488ba (MD5)
Previous issue date: 2011 / Resumo: Os mecanismos de transporte no interior do concreto são os principais responsáveis pela sua deterioração. Desta maneira, a permeabilidade deste material tem vital importância e influência na sua durabilidade, ou seja, influenciando na principal característica que determina a vida útil para o qual foi projetado. É a permeabilidade que controla a taxa de ingresso e movimentação de agentes deletérios que podem comprometer física e quimicamente a estrutura interna deste material, que pode ocasionar na deterioração da sua macro e microestrutura. Por isso, diversas metodologias têm sido empregadas para mensurar e avaliar essa propriedade do concreto; no entanto, grandes disparidades têm sido encontradas. Assim, este trabalho visa avaliar permeabilidade ao ar de concretos produzidos com cimento Portland de alto-forno (CP III - 40). O traço empregado nas séries de concreto produzidas foi nas proporções de cimento: areia: brita de 1:2:3. Foram empregadas três relações água/cimento (0,42 - 0,46 e 0,50), e os concretos submetidos à dois tipos diferentes de cura (imersa e ambiente) e ensaiados aos 7 dias, 28 dias e 350 dias. A metodologia empregada para a determinação da permeabilidade ao ar do concreto foi a metodologia proposta por Thenoz. Para complementar os resultados de permeabilidade ao ar foram realizados também ensaios para determinação do índice de vazios e absorção de água por capilaridade. Os resultados indicaram que os concretos com maiores relações água/cimento têm maiores valores de índice de vazios e apresentaram os maiores valores de absorção de água por capilaridade e permeabilidade ao ar. A cura imersa demonstrou ser mais eficaz do que a cura ambiente, pois os concretos submetidos a este tipo de cura foram os que obtiveram os menores valores de índice de vazios, absorção de água por capilaridade e permeabilidade ao ar. A idade de hidratação também influenciou nos resultados, onde idades mais avançadas também demonstraram menores valores de índice de vazios, absorção de água por capilaridade e permeabilidade ao ar. A análise da metodologia proposta por Thenoz para a mensuração da permeabilidade ao ar do concreto indicou que, de acordo com o número Mach, não há descompressibilidade do ar durante o ensaio. De acordo com o número Reynolds do escoamento, é possível afirmar que o escoamento durante o ensaio de permeabilidade ao ar proposto pela metodologia Thenoz ocorre sob regime laminar. De acordo com os resultados obtidos na análise fluido-dinâmica do escoamento, a metodologia Thenoz, para a mensuração da permeabilidade ao ar do concreto, mostrou-se eficaz para a determinação dessa propriedade do concreto / Abstract: Transport mechanisms in cement-based composites are primarily responsible for their deterioration. Thus, the permeability of cement-based materials is vital in the durability of concrete, which is the main characteristic that determines the life for which they were designed. It is the permeability, which controls the rate of entry and movement of deleterious agents that can compromise physically and chemically the internal structure of these materials, causing a deterioration of its microstructure. Several methods have been employed to measure and assess the permeability of concrete, but major differences have been found. Thus, this work is to assess the air permeability of concrete produced with Portland cement, blast furnace (CP III - 40). The dash employee in the series of concrete was produced in the proportions of cement: sand: crushed of 1:2:3. Relations have been employed three water / cement (0.42 - 0.46 and 0.50), and the concrete submitted to two different types of healing (submerged and environment) and tested at 7 days, 28 days and 350 days. The methodology used to determine the permeability of concrete was to air the methodology proposed by Thenoz. To complement the results of the air permeability were also conducted tests to determine the rate of empty and absorption of water by capillary. The results indicated that the concrete relations with major water / cement have highest rate of empty and had the highest absorption of water by capillary permeability and the air. The cure immersed proved to be more effective than cure environment, because the concrete subjected to this type of cure were those who received the lowest values of voids content, absorption of water by capillary permeability and the air. The age of hydration also influenced the results, where elderly also showed lower values of voids content, absorption of water by capillary permeability and the air. The analysis of the methodology proposed by Thenoz for the measurement of the air permeability of the concrete indicated that, according to the Mach number, there is incompressibility air during the test. In accordance with the Reynolds number of outlets, it can be said that the disposal during the testing of the air permeability methodology proposed by the Thenoz occur under laminar regime. The assessment of Thenoz methodology to measure the air permeability of concrete shows that this is an effective concrete test, according to fluid-dynamics analyzes evaluate / Mestrado / Arquitetura e Construção / Mestre em Engenharia Civil
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/257821 |
| Date | 19 August 2018 |
| Creators | Pereira, Valdir Moraes |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Camarini, Gladis, 1958-, Ducatti, Vitor Antonio, Rossignolo, João Adriano |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Civil, Arquitetura e Urbanismo, Programa de Pós-Graduação em Engenharia Civil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 136 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds