Previous issue date: 2016-12-20 / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Este estudo avaliou as propriedades mecânicas (resistência à flexão biaxial e dureza) e de superfície (rugosidade) da zircônia monolítica infiltrada com sílica, glazeada, ou polida. Foram confeccionados 198 discos de zircônia (14 mm de diâmetro, 1,2 mm de espessura). As amostras foram polidas com lixas de SiC #1200 e divididas em três grupos principais (n=66). No primeiro, os discos foram infiltrados com sílica, no segundo foram glazeados e no terceiro foram polidos com borrachas abrasivas. Após isso, foram divididos em dois subgrupos (n=33), nos quais somente um de cada tratamento foi submetido a simulação do desgaste fisiológico com esteatitas. Em seguida, as amostras foram submetidas a análises de rugosidade, dureza e ao ensaio de flexão biaxial (ISO 6872) em água. Também foram realizadas análises de difração de raios-X. Os valores de resistência (MPa) foram ranqueados e submetidos a análise de Weibull para cálculo de módulo e resistência característica dos materiais (IC 95%). As amostras também foram analisadas em microscopia eletrônica de varredura para a visualização do desgaste. Os difractrogramas mostraram que os tratamentos, glaze e infiltrado não induziram a transformação de fase, assim como o desgaste, porém o polimento induziu a formação de uma fase cúbica comprimida na superfície. A MEV mostrou as superfícies das amostras, com a formação de estrias nas amostras polidas, silicato de zircônia nas infiltradas e irregularidades nas glazeadas. Também foi possível verificar a remoção do tratamento de superfície após a simulação do desgaste. O glaze apresentou rugosidade e dureza superior, com diferença significativa, comparado aos demais tratamentos, quando não houve desgaste. Nos grupos com desgaste não houve diferença significativa. Nos resultados do teste de flexão, o grupo que apresentou a maior média foi o polido sem desgaste e após a realização da análise de Weibull, não houve diferença significativa entre eles. / This study evaluated the mechanical properties (biaxial flexural strength and hardness) and surface properties (roughness) of infiltrated, glazed or polished monolithic zirconia. 198 zirconia discs were prepared (14 mm diameter, 1,2 mm thickness). The specimens were polished with SiC abrasive paper #1200, and then specimens were divided into three main groups (n=66). In the first, the discs were infiltrated with silica, in the second were glazed and and in third were polished with abrasive rubbers. Thereon, were divided into two subgroups (n=33), in which only one group of each treatment was subjected to wear with steatite, in order to simulate the physiological wear. The specimens were then subjected to roughness analysis, hardness and biaxial bending test (ISO 6872) immersed in water. The groups were evaluated by x-ray diffraction (XRD). The strength values (MPa) were ranked and subjected to Weibull analysis to calculate the Weibull modulus and characteristic strength of the material (CI 95%). The samples were also analyzed by SEM to visualize the wear. In the XRD, it was showed that the treatments did not induce phase transformation as well as wear, however the polishing induced the formation of a compressed cubic phase on the surface. SEM showed the surfaces of the samples with grooves formation on polished, zirconium silicate on infiltrated and irregularities on glazed. It was also possible to verify the removal of surface treatment after simulated wear. The glaze showed higher roughness amd hardness, with a significant difference compared to the other treatments, when there was no wear. In groups with wear there was no significant difference. The results of the bending test, the group with the highest average was polished without wear and after the Weibull analysis, there was no significant difference among them. / FAPESP: 2015/11405-7
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/148610 |
| Date | 20 December 2016 |
| Creators | Alves, Larissa Marcia Martins [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Marinho, Renata Marques de Melo [UNESP], Campos, Tiago Moreira Bastos [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 600 |
Page generated in 0.0029 seconds