Previous issue date: 1995 / Resumo: Este trabalho teve como objetivo verificar o efeito do meio bucal simulado sobre a força de tração exercida por 15 cadeias elastoméricas coloridas, de fabricação brasileira (Tecnident), em função do tempo de distensão. As amostras foram constituídas de 10 módulos, de 4 anéis, para cada cor, selecionados ao acaso. Os módulos foram distendidos à distância constante de 25 mm., imersos em saliva artificial (Oralub) e mantidos em estufa, à temperatura constante de 37°C ± 1 °C. As leituras de força de tração foram efetuadas com um dinamômetro Correx (Suíça), obedecendo a 10 períodos de tempo: inicial, 1 hora, 6 horas, 12 horas, 24 horas, 72 horas, 1 semana, 2 semanas, 3 semanas e 4 semanas. Os resultados mostraram, que as cadeias elastoméricas se comportaram diferentemente entre si, quanto à força de tração, variando de intensidade conforme a sua cor. Assim, a força inicial variou de 459,0 gramas (verde 1) a 345,0 gramas (verde 3) e a força remanescente, ao final de 4 semanas de teste, variou de 162,0 gramas (cinza) a 94,0 gramas (verde 3). Ao final de 4 semanas de teste, a maior porcentagem de força remanescente foi apresentada pelo elastômero de cor pink, com 41,14%, enquanto a menor foi apresentada pelo elastômero de cor verde 1, com apenas 22,77% de força remanescente. Portanto, após a análise estatística dos resultados, foi possível concluir que o meio bucal simulado exerceu efeito significativo sobre o desempenho da força de tração das cadeias elastoméricas pigmentadas, de fabricação brasileira, após distensão / Abstract: This work has as goal to check the effect of simulated buccal surrounding on the traction force made by 15 colorful elastomeric chains, Brazilian production (Tecnident), in function of distension time. The samples were made from 10 modules, of 4 rings for each color, selected at random. The modules were distended to the constant distance of 25 mm., immersed in artificial saliva (Oralube) and kept in sterilizer at the constant temperature of 35°C ± 1°C. The traction force readings were with a dynamometer Correx (Swiss), following the 10 time periods: initial, 1 hour, 6 hours, 12 hours, 24 hours, 72 hours, 1 week, 2 weeks, 3 weeks and 4 weeks. The results showed that the elastomeric chains behaved differently among themselves, as the traction force, changing of intensity, depending on its color. In this way, the initial force varied from 459,0 grams (green 1) to 345,0 grams (green 3) and the remaining force, at the end of 4 week's test varied from 162,0 grams (gray) to 94,0 grams (green 3). At the end of 4 week's test, the higher percentage of remaining force was showed by the pink elastomer, with 41,14% while the lowest one was showed by the green 1 elastomer, with just 22,77% of remaining force. Therefore, after the result statistical analyze, was possible to verify that the simulated buccal surrounding made meaningful effect over the traction force performance of pigmented elastomeric chains, Brazilian production, after distension / Doutorado / Ortodontia / Doutor em Ciências
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290064 |
Date | 21 July 2018 |
Creators | Almeida, Renato Castro de |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Simonides, 1939- |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Ciências |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 105f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0014 seconds