The main aim of this work was to develop a method of screening HgCdTe materials for carrier concentration and mobility using Faraday rotation θ and absorption α. Faraday rotation provides N/m*2, where N is the carrier concentration and m* is the effective mass. Since m* was not known in HgCdTe, a Faraday rotation spectrometer was developed to systematically measure it as a function of temperature and Cd mole fraction. Effective masses in n-InSb, and n-GaAs were measured and compared with known values in the literature to validate the method. Mobility is proportional to θ/α. The proportionalities were determined in HgCdTe, n-InSb, and n-GaAs at infrared wavelengths.
| Identifer | oai:union.ndltd.org:LABT_ETD/oai:elaba.lt:LT-eLABa-0001:E.02~2006~D_20060512_152126-98689 |
| Date | 12 May 2006 |
| Creators | Clarke, Frederick Walter |
| Contributors | Laurinavičius, Albertas, Bendorius, Rimgaudas Adolfas, Balevičius, Saulius, Vaičikauskas, Viktoras, Ašmontas, Steponas, Godlewski, Marek, Tamulevičius, Sigitas, Babonas, Gintautas Jurgis, Vilnius Gediminas Technical University |
| Publisher | Lithuanian Academic Libraries Network (LABT), Vilnius Gediminas Technical University |
| Source Sets | Lithuanian ETD submission system |
| Language | Lithuanian |
| Detected Language | English |
| Type | Doctoral thesis |
| Format | application/pdf |
| Source | http://vddb.library.lt/obj/LT-eLABa-0001:E.02~2006~D_20060512_152126-98689 |
| Rights | Unrestricted |
Page generated in 0.0018 seconds