Ferroelectric oxides are a group of advanced electronic materials with a wide variety of properties useful in applications such as memory devices, resonators and filters, infrared sensors, microelectromechanical systems, and optical waveguides and modulators. Among the oxide perovskite-structured ferroelectric thin film materials, sodium potassium niobate or Na0.5K0.5NbO3 (NKN) has recently emerged as one of the most promising materials in radio frequency (rf) and microwave applications due to high dielectric tenability and low dielectric loss. This thesis presents results on growth and structural, optical, and electrical characterization of NKN thin films. The films were deposited by rf-magnetron sputtering of a stoichiometric, high density, ceramic Na0.5K0.5NbO3 target onto single crystal LaAlO3 (LAO), Al2O3 (sapphire), SrTiO3, and Nd:YAlO3, and polycrystalline Pt80Ir20 substrates. By x-ray diffractometry, NKN films on c-axis oriented LaAlO3, SrTiO3 and Nd:YAlO3 substrates were found to grow epitaxially, whereas films on r-cut sapphire and polycrystalline Pt80Ir20 substrates were found to be preferentially (00l) oriented. The surface morphology was explored using atomic force microscopy. Optical and waveguiding properties of the Na0.5K0.5NbO3/substrate heterostructures were characterized using prism-coupling technique. Sharp and distinguishable transverse magnetic and electric propagation modes were observed for NKN thicknesses up to 2.0 μm. The extraordinary and ordinary refractive indices were calculated together with the birefringence of the NKN material. The electro-optic effect in transverse geometry was measured in transmission, where the effective linear electro-optic response was determined to reff = 28 pm/V for NKN/Al2O3 with an applied dc field up to 18 kV/cm. The ferroelectric state in NKN films on Pt80Ir20 at room temperature was indicated by a polarization loop with saturated polarization as high as 33.4 μC/cm2 at 700 kV/cm, remnant polarization of 10 μC/cm2, and coercive field of 90 kV/cm. Current-voltage characteristics of vertical Au/NKN/PtIr capacitive cells and planar Au/NKN/LAO interdigital capacitors (IDCs) showed very good insulating properties, with the leakage current density for an NKN IDC on the order of 30 nA/cm2 at 400 kV/cm. Rf dielectric spectroscopy demonstrated low loss, low frequency dispersion, and high voltage tunability. At 1 MHz, NKN/LAO showed a dissipation factor tan δ = 0.010 and a tunability of 16.5 % at 200 kV/cm. For the same structure the frequency dispersion was Δεr = 8.5 % between 1 kHz and 1 MHz. / QC 20100928
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-193 |
Date | January 2005 |
Creators | Blomqvist, Mats |
Publisher | KTH, Mikroelektronik och Informationsteknik, IMIT, Stockholm : KTH |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | Trita-FYS, 0280-316X ; 5299 |
Page generated in 0.0018 seconds