The aims of this thesis are fabrication of Ti/APC-2 hybrid nanocomposite laminates and investigation of their mechanical properties at elevated temperature. The prepregs of APC-2 were stacked into cross-ply [0/90]s and quasi-isotropic [0/45/90/-45] laminates spread uniformly with nanoparticles SiO2. The sheet surface was treated by chromic acid anodic method to achieve perfectly bonding with matrix PEEK. The prepregs were sandwiched with the Ti alloy sheets. The modified diaphragm curing process was adopted to produce Ti/APC-2 hybrid nanocomposite laminates. The nanocomposite laminates were a five-layer composite with two 0.55 mm thick APC-2 layers sandwiched by three 0.5 mm thick Gr.1 titanium alloy sheets. The MTS 810 material testing machine was used to conduct the tension and fatigue tests. In addition, the MTS 651 environmental chamber was installed to control and keep the experimental temperature, such as 25¢XC, 75¢XC, 100¢XC, 125¢XC and 150¢XC.
The mechanical proper¬ties, such as ultimate tensile strength, longitudinal stiffness of cross-ply and quasi-isotropic nanocomposite laminates, were obtained from the static tensile test. The stress-strain diagrams were plotted in the corresponding temperature. The constant stress amplitude tension-tension cyclic tests were carried out by using load-control mode at a sinusoidal loading with frequency of 5Hz and stress ratio R=0.1. The received fatigue data were plotted in normalized S-N curves at variously elevated temperature.
From the summarized results, some conclusions were made. First, the ultimate strength of Ti/APC-2 nanocomposits was better than Ti/APC-2 composites at room temperature; Second, Both two type nanocomposite laminates¡¦ ultimate strength and S-N curves go downwards as temperature rising, especially at 150¢XC; Third, The fatigue tensile strength of both hybrid composite laminates was the lowest at 150¢XC. Fourth, Ti/APC-2 quasi-isotropic nanocomposite laminates had better fatigue resistance than Ti/APC-2 cross-ply nanocomposite laminates. Finally,The longitudinal stiffness was in good agreement with prediction by using the modified ROM because of the changed curve fitting ranges.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0823110-172124 |
| Date | 23 August 2010 |
| Creators | Chang, Che-kai |
| Contributors | Kung H.K., Shin-Pon Ju, Ming-Hwa R. Jen, Ming Chen, C. F. Liu |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0823110-172124 |
| Rights | restricted, Copyright information available at source archive |
Page generated in 0.0019 seconds