Estudo das propriedades elétro-óptica de dispositivos eletroluminescentes confeccionados com um compósito híbrido

Made available in DSpace on 2014-06-11T19:25:31Z (GMT). No. of bitstreams: 0
Previous issue date: 2009-10-05Bitstream added on 2014-06-13T18:53:36Z : No. of bitstreams: 1
stefanelo_jc_me_rcla.pdf: 1971755 bytes, checksum: f2545c6a190dc7a872bf14f2c2b4fce6 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Neste trabalho foi desenvolvido um dispositivo eletroluminescente (EL) constituído de um compósito híbrido (CH), formado por uma blenda polimérica e um material EL inorgânico. A blenda é composta por um polímero condutor, a poli(o-metoxianilina) (POMA) dopada com ácido tolueno sulfônico (TSA), e um polímero isolante, o poli(fluoreto de vinilideno-co-trifluoretileno) (P(VDF-TrFE)). A esta blenda é acrescentado um material EL inorgânico, o silicato de zinco dopado com Manganês (Zn2SiO4:Mn), formando assim, o compósito híbrido. O dispositivo foi construído depositando o compósito por drop casting sobre um substrato de óxido de estanho dopado com flúor (FTO) e após cristalização em uma estufa foi depositado um eletrodo de metal por evaporação à vácuo formando uma estrutura tipo “sanduíche”. Neste trabalho foram construídos dispositivos com eletrodo superior de Alumínio (Al) e Ouro (Au), denominados: FTO/CH/Al e FTO/CH/Au. O comportamento elétrico dos dispositivos de FTO/CH/Al foram analisados aplicando-se as teorias de Emissão Termoiônica, Emissão Schottky e Emissão Poole-Frenkel, o que tornou possível encontrar alguns parâmetros como: altura da barreira para a junção metal/CH, condutividade do CH e fator de retificação. O dispositivo de FTO/CH/Au foi caracterizado pela técnica de espectroscopia de impedância, sendo obtido também a altura da barreira para a junção metal/CH, a condutividade do CH, além da constante dielétrica do compósito e como variam esses dois últimos parâmetros com a temperatura. A aplicação das teorias de Emissão Termoiônica, Emissão Schottky e Emissão Poole-Frenkel produziram resultados semelhantes aos obtidos pela técnica de espectroscopia de impedância. Os espectros de luminescência apresentaram um pico em l = 528 nm com estabilidade temporal de emissão comparável a dos dispositivos inorgânicos puros. / In this work was developed an electroluminescent (EL) device made up with a hybrid composite (CH), that is formed by a polymeric blend and an inorganic EL material. The conductive polymer, poly(o-methoxyaniline) (POMA) doped with p-Toluene sulphonic acid (TSA), and an isolating polymer, the poly(vinylidenefluoride-co-trifluoroethylene) (P(VDFTrFE)), was used to make the polymer blend. An inorganic EL material, the zinc silicate manganese-doped (Zn2SiO4:Mn), was added to the blend, forming the hybrid composite. The composite was deposited by drop-casting over a Fluoride Tin Oxide substrate (FTO) and after the crystallization in an oven a metal electrode was deposited by vacuum evaporation, forming a type “sandwich” structure. In this work were constructed different devices. Aluminum (Al) and Gold (Au) were used as upper electrodes, therefore the device structures were: FTO/CH/Al and FTO/CH/Au. To analyze the electrical behavior of the FTO/CH/Al device was applied the theories of Thermionic Emission, Schottky Emission and Poole- Frenkel Emission. Using these theories was possible to obtain parameters such as; the barrier height from the metal/CH junction, CH conductivity and diode rectifier factor. The FTO/CH/Au device was characterized using the impedance spectroscopy technique. For this device was also possible to obtain the barrier height from the metal/CH junction, CH conductivity and CH dielectric constant. For the last two parameters the dependence with the temperature were also observed. The application of the theories of Thermionic Emission, Schottky Emission and Poole-Frenkel Emission produced similar results to that obtained by the impedance spectroscopy technique. The luminescence spectra, for the devices, showed a peak at l = 528 nm with emission stability in time that it is comparable of pure inorganic devices.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/91900
Date05 October 2009
CreatorsStefanelo, Josiani Cristina [UNESP]
ContributorsUniversidade Estadual Paulista (UNESP), Chinaglia, Dante Luis [UNESP]
PublisherUniversidade Estadual Paulista (UNESP)
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format77 f. : il., tabs.
SourceAleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP
Rightsinfo:eu-repo/semantics/openAccess
Relation-1, -1

Page generated in 0.0028 seconds