Objetivo: El presente estudio in vitro compara la resistencia al cizallamiento de los cementos resinosos RelyX U200 (3M ESPE), MultilinkAutomix (IvoclarVivadent) y Allcem dual (FGM) en la interfase cerómero/dentina erosionada con la bebida carbonatada Coca Cola®. Materiales y métodos: El diseño del estudio fue de tipo experimental in vitro. El tamaño muestral fue de 66 dientes bovinos, los cuales fueron seleccionados y cortados. Se expuso la dentina con lijas de diferentes granos y se confeccionó las bases de acrílico transparente. Se distribuyó en 3 grupos (n=22): RelyX U200 (3M ESPE), MultilinkAutomix (Ivoclar Vivadent) y Allcem dual (FGM). Se confeccionó cilindros de cerómero (4mm de diámetro y 6mm de altura) SR NEXCO (Ivoclar Vivadent), seguidamente fueron arenados. El desafío erosivo consistió en sumergir los especímenes en la bebida carbonatada Coca Cola® durante tres ciclos de inmersión de 5 minutos al día durante5 días. La cementación de los bloques de cerómero a la dentina erosionada se realizaron según la indicación de cada fabricante. Las muestras se almacenaron en una estufa a 37°Ccon suero fisiológico al 0.09% por 24 horas. El análisis de los valores de cizallamiento se realizó con la máquina de ensayo universal (Instrom®) en MPa (a una velocidad de 5mm/1min).Los resultados (media, desviación estándar) fueron realizados mediante estadística descriptiva y la comparación de la resistencia al cizallamiento fue analizada con la prueba Kruskal-Wallis seguida por una prueba de post-hoc con ayuda del comando Kruskal Wallis 2 en Stata®. Resultados: Las medias y desviación estándar encontradas fueron cemento MultilinkAutomix (2,7±0,59), cemento RelyX U200(1,41±0,26) y el cemento Allcem dual (0,92±1,17). Se encontraron diferencias estadísticamente significativas (p=0.0001) al comparar la resistencia adhesiva de los tres cementos resinosos. En la prueba de post hoc de los tres cementos resinosos se encontraron que las tres diferencias son estadísticamente significativas (p <a 0,001 en los tres cementos resinosos). Conclusión: Bajo condiciones in vitro, el cemento MultilinkAutomix (IvoclarVivadent) obtuvo mejores resultados de resistencia adhesiva en dentina erosionada. / Objective: The aim of this study was to compare the shear bond strength of three resin cements RelyX U200 (3M ESPE), Multilink Automix (IvoclarVivadent) and Allcem dual (FGM) at the ceromer/dentine eroded interface with the Coca Cola® carbonated beverage. Materials and methods: The present study was experimental type in vitro. The sample size was 66 bovine teeth, which were selected and cut. The dentin was exposed with different grains of sandpaper and the transparent acrylic bases were made. The specimens were distributed in 3 groups (n = 22): RelyX U200 (3M ESPE), Multilink Automix (IvoclarVivadent) and Allcem dual (FGM). Ceromer cylinders (4mm diameter and 6mm height) were made with SR NEXCO (IvoclarVivadent), then sandblasted before the cementation. The erosive challenge in vitro was realized in 3 times/5minutes per day/5 days in Coca Cola® soft drink. SR NEXCO (Ivoclar Vivadent) blocks were cemented to the eroded dentin, according to the manufacturer's instructions. The samples were stored in 0.09% physiological saline at 37 °C for 24 hours. The analysis of the shear values was performed with a universal test machine (Instrom®) in MPa (at a speed of 5mm/1 min).The results (mean, standard deviation) were analyzed by descriptive statistics and the comparison of the shear strength was analyzed with the Kruskal-Wallis test followed by a post-hoc test with the help of the Kruskal Wallis 2 command in Stata®. Results: There were statistically significant differences (p=0.0001) among the resin cements evaluated. The means were Multilink Automix (2.7 ± 0.59), RelyX U200 (1.41 ± 0.26) and Allcem dual (0.92 ± 1.17). In the post hoc test of the cements RelyX U200 (3M ESPE), there was statistically significant (p <0.001). Conclusion: Under in vitro conditions, Multilink Automix cement got better results of bond strength in eroded dentin. / Tesis
| Identifer | oai:union.ndltd.org:PERUUPC/oai:repositorioacademico.upc.edu.pe:10757/625108 |
| Date | 05 December 2018 |
| Creators | Cuarez Quispe, Pamela Milagros, Huaman Callalli, Pedro Josue |
| Contributors | Casas Apayco, Leslie Caroll |
| Publisher | Universidad Peruana de Ciencias Aplicadas (UPC) |
| Source Sets | Universidad Peruana de Ciencias Aplicadas (UPC) |
| Language | Spanish |
| Detected Language | Spanish |
| Type | info:eu-repo/semantics/bachelorThesis |
| Format | application/pdf, application/epub, application/msword |
| Source | Universidad Peruana de Ciencias Aplicadas (UPC), Repositorio Académico - UPC |
| Rights | info:eu-repo/semantics/openAccess, Attribution-NonCommercial-ShareAlike 3.0 United States, http://creativecommons.org/licenses/by-nc-sa/3.0/us/ |
Page generated in 0.0026 seconds