Previous issue date: 2016-12-21 / O sulfeto de zinco (ZnS) é um excelente semicondutor, com aplicações interessantes nos campos da ótica e da elétrica, mas outras propriedades como a ação como aditivo em matrizes poliméricas ainda não são muito claras em estudos anteriores. Neste trabalho, o ZnS foi sintetizado pela rota sonoquímica e nanopartículas com diâmetros de aproximadamente 2 nm foram obtidas. O ZnS produzido foi adicionado à matriz de Poli(cloreto de vinila) nas concentrações de 0,10; 0,30; 0,50; 0,70 e 1,00% (m/m). As amostras foram irradiadas com fonte de radiação gama (60Co) na dose de 25 kGy à temperatura ambiente e no ar. Análises viscosimétricas mostram decréscimo na massa molar viscosimétrica (Mv) das amostras de PVC e PVC com ZnS (PVC/ZnS). Contudo, somente as amostras de PVC com a concentração de 0,7% de ZnS mostraram proteção molecular à matriz polimérica. As interações entre o ZnS e o PVC, constatadas por espectros de FT-IR, favoreceram a ação do ZnS como agente proteto radiolítico do PVC. Estes resultados sugerem o uso de nanopartículas de ZnS, sintetizadas pela rota sonoquímica, como um novo aditivo na matriz de PVC para aplicações de resistência à irradiação gama. / Zinc sulfide (ZnS) is an excellent semiconductor, with interesting applications in the optical and electrical fields, but other properties, such as the action as additive in polymer matrices, are still not very evident in previous studies. In this work, the ZnS was synthesized by sonochemical method and nanoparticles with diameters around 2 nm were obtained. The ZnS produced was added to the Poly (vinyl chloride) matrix at concentrations of 0.10; 0.30; 0.50; 0.70 and 1.00% (m/m). The samples were irradiated with gamma radiation (60Co) at dose of 25 kGy in air at room temperature. Viscosimetric analysis show a decrease in viscosity-average molar mass (Mv) of PVC and PVC with ZnS (PVC/ZnS) samples. However, only the PVC/ZnS samples with 0.7% concentration of ZnS showed molecular protection to the polymer matrix. The interactions between ZnS and PVC, verified by FT-IR spectra, favored the action of ZnS as a radiolytic protective agent of PVC. These results suggest the use of sonochemically synthesized ZnS nanoparticles as a new additive in the PVC matrix for gamma irradiation resistance applications.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpe.br:123456789/24777 |
Date | 21 December 2016 |
Creators | SILVA, Roberta Cristina da |
Contributors | http://lattes.cnpq.br/2139448380426938, AQUINO, Kátia Aparecida da Silva, SANTOS, Renata Francisca da Silva |
Publisher | Universidade Federal de Pernambuco, Programa de Pos Graduacao em Tecnologias Energeticas e Nuclear, UFPE, Brasil |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UFPE, instname:Universidade Federal de Pernambuco, instacron:UFPE |
Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds