Previous issue date: 2018-02-02 / O desperdício de materiais na construção civil é crescente e isso é um problema para promoção do desenvolvimento sustentável. Por isso, são importantes pesquisas que apontem soluções inovadoras no uso de descartes, principalmente em países como o Brasil, onde o desperdício nesta área é de cerca de 30% e o país precisa se desenvolver e utilizar com equilíbrio seus recursos naturais e energéticos. O objetivo da pesquisa foi desenvolver um tipo de fulget para revestimentos de paredes externas, feito com cimento branco, pó de rocha calcária, e com cargas minerais derivadas dos rejeitos da areia peneirada e sem pigmentação. Trata-se de pesquisa experimental, por isso foi construída uma célula de teste, e numa parede
externa voltada para o poente, onde se tem elevada incidência de radiação solar diária, foram instalados revestimentos com fulget e com reboco, com as mesmas dimensões, para permitir comparações. Também foi desenvolvido um sistema de medição e aquisição de dados (SMAD) para medir as principais propriedades de interesse e realizar comparativamente a análise térmica dos dois revestimentos, também foram observados a evolução de problemas mecânicos e de aparência resultados da ação das intempéries sobre os revestimentos. Os resultados obtidos mostraram que o valor da refletância média (ρf=0,614) para o fulget é maior do que o valor da refletância média (ρr=0,590) para o reboco. Por outro lado, o revestimento fulget tem comparativamente menor absortância. Para a condutividade térmica, o resultado obtido para o fulget foi bem menor do que o valor para o reboco. Isso mostra que
o revestimento fulget tem maior característica isolante. Os valores da condutividade térmica média obtidos para o fulget e reboco foram respectivamente 0,285 W/mK e 0,720 W/mK. O revestimento fulget apresentou maior resistência à ação das intempéries, para as mesmas condições ambientais e temporais típicas da cidade de Campina Grande, PB. Como conclusão, é possível afirmar que o revestimento fulget desenvolvido se mostrou adequado para ser usado como revestimento externo. / The amount of civil construction wastes has been growing and that is a problem for the promotion of the sustainable development. As such it is needed to support research that lead to innovative solutions in the use of such discarded materials, mainly in countries like Brazil, which needs to develop itself and use the available energy and natural resources in a balanced way. Within this context, the research here presented contributes to a better and sustainable country. The main aim of the research was to develop a kind of fulget for external coating, whose composition is made of white cement, calcareous dust but with mineral loads derived from the tailings of sifted sand and with natural pigmentation. This is an experimental thesis and as such the methodology used consisted in building up a testing cell and install the fulget and the plaster on a wall facing the west direction and receiving a huge amount of daily solar insulation. A data acquisition system was also developed to measure the main relevant properties and allow the thermal comparison between the two coatings, also observing the evolution of mechanical and deterioration problems that appeared due to the action of the conditions to which the material was exposed. The results obtained showed that the average reflectance (ρf=0,614) for the fulget is higher than the average reflectance for the plaster (ρr=0,590). On the other hand, the fulget coating has lesser absorbance. For the thermal conductivity, the results showed that the value for the fulget is way lesser than the value for the plaster. This shows that the first one has a higher performance in thermal insulation than the last one. The average thermal conductivity for the fulget and plaster were 0.285 W/mK and 0.720 W/mK, respectively. The results also showed that the fulget coating presents higher resistance to the actions of the nature than the plaster coating, considering the same environmental and weather conditions that are expected to take place in the city of Campina Grande, PB. As conclusions it is possible to affirm that the fulget coating showed itself suitable to be used as external coating.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1507 |
| Date | 20 August 2018 |
| Creators | ROCHA, Adjalmir Alves. |
| Contributors | GRILO, Marcelo Bezerra., RODRIGUES, John Kennedy Guedes., LIMA, Wellington Sousa., MEIRA, Celeide Maria Belmont Sabino., NUNES, Antônio Gomes., LIMA, Antonio Gilson Barbosa de. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA DE PROCESSOS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.004 seconds