Activities of Cu₂O in PbO - Cu₂O - SiO₂ slags have been measured by a slag-metal equilibrium.
Excess properties of the cation were established from Temkin's
rule using the measured Cu₂O and aO²⁻ data. Lnɤ Cu⁺ values were found to
be directly proportional to the activities of silicate anions along lines of
constant NPb²⁺/NCu⁺ ratio. Also, it was observed that the excess properties of the copper cation increase with cation dilution. These properties are generally characteristic of all metal cations in PbO-Cu₂O-SiO₂ and CaO-FeO-SiO₂ slags.
A method has been devised for interpolation and extrapolation of measured activity data in ternary silicate slag systems.
Integration of the cationic form of the Gibbs-Duhem equation in the PbO-Cu₂O-SiO₂ system has shown Toop's method of calculating ternary oxygen ion activities to be satisfactory.
Agreement of the measured-cationic data with other data in the PbO-Cu₂O-SiO₂ system is good. The established cationic excess properties are structurally interpretable indicating that anionic and cationic activities, as predicted from ionic theory, are reasonable. / Applied Science, Faculty of / Materials Engineering, Department of / Graduate
| Identifer | oai:union.ndltd.org:UBC/oai:circle.library.ubc.ca:2429/39646 |
| Date | January 1962 |
| Creators | Forward, Gordon Edward |
| Publisher | University of British Columbia |
| Source Sets | University of British Columbia |
| Language | English |
| Detected Language | English |
| Type | Text, Thesis/Dissertation |
| Rights | For non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use. |
Page generated in 0.0016 seconds