Orientador: Reiko Sato Turtelli / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-07-14T04:17:13Z (GMT). No. of bitstreams: 1
Sinnecker_JoaoPaulo_M.pdf: 3478983 bytes, checksum: e5da519c6d7c80bf8c1cf6b509b439cc (MD5)
Previous issue date: 1992 / Resumo: Foram feitas medidas permeabilidade inicial (m ) e de campos críticos (Hp) em fitas de liga amorfa de composição nominal CO70.4Fe4.6Si15B10, em função da temperatura e de campos magnéticos ac aplicados. Para isso foi construído um forno que permite tratamentos térmicos a temperatura constante e, à taxas de aquecimento constantes. As medidas de permeabilidade inicial foram feitas com campos magnéticos H constantes, variando-se a temperatura entre a temperatura ambiente (Tamb) e a temperatura de Curie (Tc) e vice-versa. Os campos críticos foram determinados através das curvas de permeabilidade inicial em função de H, para uma dada temperatura constante. As amostras foram analisadas com difratogramas de Raios-X, depois de todos os tratamentos térmicos, para assegurar a amorficidade das mesmas. Os resultados mostram que existe uma súbita, mudança em m, à temperaturas características, dependentes do campo aplicado H. Saltos na permeabilidade inicial em valores característicos de Hp nas Curvas de m x H também foram observados. Estes resultados podem ser explicados por meio de fenômenos envolvendo "pinning" de paredes de domínios, causados por anisotropias locais induzidas por ordenamento de pares atômicos e tensões localizadas / Abstract: Measurements of initial magnetic permeability (m ) and critical fields (Hp) were performed in ferromagnetic amorphous ribbons of nominal composition CO7O.4Fe4.6Si15B10, as a function of temperature and applied magnetic field. A furnace that allow thermal treatments at constant heating rate, was contructed. The initial permeability rneasurements were performed with constant magnetic applied field H, and temperature varying from room temperature (Tamb) to Curie temperature (Tc) and vice-versa. The critical fields were found from the initial permeability as a function of applied field curves, for a constant temperature. The samples were analyzed with X-ray difratometer to ensure amorphicity. The results shown suden jumps in m at characteristic temperatures which depends on the applied field H. Suden jumps in the initial permeability at characteristic values of Hp in the m x H curves, were also observed. These results can be explain by domain wall "pinning" effect caused mainly by local anisotropy induced by atomic pair ordering and local stresses / Mestrado / Física / Mestre em Física
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/277053 |
| Date | 15 June 1992 |
| Creators | Sinnecker, João Paulo |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Turtelli, Reiko Sato, Turtellil, Reiko Sato, Silva, Edison Zacarias da, Missel, Frank Patrick |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Física Gleb Wataghin, Programa de Pós-Graduação em Física |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | [77]f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds