Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2017. / Made available in DSpace on 2017-05-31T14:18:09Z (GMT). No. of bitstreams: 1
345988.pdf: 3518006 bytes, checksum: 67aafb150b62a10d71aaf83c5bbc7225 (MD5)
Previous issue date: 2017 / O objetivo do presente estudo in vitro foi comparar a adaptação em esmalte e dentina, o selamento marginal e o nível de manchamento superficial de 2 resinas compostas de diferentes percentuais de contração de polimerização (Charisma Diamond e Filtek Z350) em facetas diretas de resina composta depois de serem submetidas a pigmentação extrínseca e ciclagem térmica. Trinta e dois incisivos inferiores, preparados para receber facetas diretas de resina composta foram divididos aleatoriamente em 4 grupos (n= 8): os Grupos 1 e 3 foram restaurados com resina composta nanohíbrida de baixa contraçao de polimerizaçao e os grupos 2 e 4 foram restaurados com resina composta nanoparticulada (com contraçao de polimerizaçao normal). Com o objetivo de avaliar o nível de manchamento superficial, os Grupos 1 e 2 foram armazenados em vinho tinto por 14 dias a 37°C e foram registrados fotograficamente antes e após a pigmentação extrínseca. Os registros fotográficos foram anexados a questionários de avaliação, submetidos a 2 examinadores voluntários (cirurgiões-dentistas). A seguir, os espécimes dos 4 grupos foram submetidos a 5.000 ciclos térmicos, a nanoinfiltração foi observada usando microscopia eletrônica de varredura (MEV), no modo retroespalhado e com espectometria de energia dispersiva. a percentagem de nanoinfiltração de partículas de prata na interface dente/restauração foi calculada usando um programa de análise digital de imagens. Os resultados foram tabulados e analisados estatisticamente por ANOVA e pelos testes de Kruskal Wallis e Mann Withney, com nível de significância de a =0,05. Observou-se que houve diferença significativa entre a infiltração na margem cervical (dentina) e infiltração total nos quatro grupos, assim como, diferença significativa entre a margem incisal (esmalte) e na margem cervical (dentina) em todos os grupos. Foi observado absorção de prata na margem cervical em todos os grupos, com maior percentagem de infiltração encontrada no Grupo 1. Não houve diferença estatística significativa entre os grupos da margem incisal (esmalte). As facetas diretas de resina composta nanoparticulada apresentaram melhor selamento em esmalte e dentina quando comparados com resina composta nanohíbrida. A resistência ao manchamento superficial parece ser semelhante em ambos as resinas compostas. Oconsumo simulado de vinho causa manchamento superficial nas facetas de resina composta.<br> / Abstract : The aim of this in vitro study was to compare the adaptation to enamel and dentin, the marginal sealing and the level of surface staining of 2 composite resins of different percent polymerization shrinkage (Charisma Diamond and Filtek Z350) in direct composite laminate veneers after being subjected to extrinsic pigmentation and thermal cycling. Thirty-two mandibular incisors, prepared to receive direct composite laminate veneers, were randomly divided into 4 groups (n = 8): Groups 1 and 3 were restored with a nanohybrid composite resin and Groups 2 and 4 were restored with a nanoparticulate composite resin. In order to evaluate the degree of surface staining, Groups 1 and 2 were stored in red wine for 14 days at 37 °C and were photographed before and after extrinsic pigmentation. The photographic records were attached to 5 evaluation scores, submitted to 2 voluntary examiners (dental surgeons). The specimens of the four groups were sectioned and immersed into silver nitrate solution after aging with 5,000 thermocycles. Nanoleakage was observed using a scanning electron microscopy (SEM), in both backscattered electron mode and EDX spectrometry dispersive mode; the percentage distribution of silver particles at the restoration/tooth interface was calculated using a digital image analysis software. The results were plotted and analyzed statistically using one-way ANOVA, and Kruskal Wallis and Mann Whitney?s tests. The level of significance was set to a =.05. Statistically significant differences were observed between dentin infiltration and total infiltration in the four groups, as well as, significant differences between enamel and dentin in all groups. It was observed clear silver uptake at the cervical margin in the four groups, with the highest microleakage percentage found in Group 1. No significant differences were observed in enamel between the four Groups. Direct composite laminate veneers of nanoparticles resin, presented better enamel and dentine adaptation when compared with direct composite laminate veneers of nanohybrid resin. The resistance to surface staining seemed to be similar in both tested groups.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/176062 |
| Date | January 2017 |
| Creators | Diaz, Sheila Francesca Rabanal |
| Contributors | Universidade Federal de Santa Catarina, Lopes, Guilherme Carpena, Bernardon, Jussara Karina |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 140 p.| il., gráfs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0128 seconds