Previous issue date: 2016-01-28 / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / O objetivo desse trabalho foi identificar por meio da utilização de geometrias complexas (pela análise de elemento finito) e simplificadas, se novas tecnologias (sistema CAD/CAM) resultam em um comportamento biomecânico mais favorável na cerâmica de cobertura quando comparado à técnica de aplicação convencional (estratificação). Foram modelados três diferentes estruturas de prótese parcial fixa de três elementos com diferentes técnicas de fabricação: convencional, Rapid Layer (feldspática, cimento resinoso e zircônia) e CAD-on (dissilicato, material vítrio de baixa fusão e zircônia) a fim de analisar a distribuição tensão de tração gerada durante um ensaio mecânico pelo método por elementos finitos. Discos (cerâmica de cobertura e zircônia) foram unidos seguindo as três diferentes técnicas (convencional, Rapid Layer e CAD-on). Foram também confeccionadas próteses parciais fixas de 3 elementos pela técnica de multicamada seguindo as mesmas configurações dos modelos utilizados na análise por elementos finitos. Essas coroas foram cicladas durante 2x106 ciclos para analisar falhas na cerâmica de cobertura, como trincas, lascamento, delaminação e falha catastrófica. Os resultados mostraram que as coroas confeccionadas com cerâmica de dissilicato de lítio e material vítreo na interface infraestrutura/cerâmica de cobertura apresentaram menor concentração de tensão de tração quando comparadas aos modelos confeccionados pela técnica convencional, que demonstraram maior concentração de tensão de tração entre as camadas (cerâmica de cobertura, interface e infraestrutura). Para os discos, o acréscimo de material na interface cerâmica de cobertura e infraestrutura mostrou maior resistência à fratura biaxial e menor propagação da trinca entre as camadas de cerâmica. As coroas cicladas não apresentaram falhas como: trincas, lascamento, delaminação e catastrófica nos primeiros 500.000 ciclos. Porém, as próteses confeccionadas com cerâmica feldspática apresentaram trincas a partir de 1x106 ciclos, diferentemente das coroas confeccionadas na técnica Rapid Layer e CAD-on. As coroas confeccionadas pela técnica RL e CAD-on podem ser consideradas um sistema favorável por prevenir a propagação de trincas radiais em direção à superfície da restauração e melhorar a tenacidade à fratura do material. / The aim was to identify whether the CAD/CAM approach resulted in more favourable stressing patterns in the veneer-ceramic when compared with a conventionally sintered Y-TZP core/veneer-ceramic. Three different designs crowns of prosthesis with three elements and different manufacturing techniques were modeled: conventional technique, Rapid Layer (feldspathic ceramic, resin cement and zirconia) and CAD-on (disilicate, fusion glass ceramic and zirconia) techniques to analyze the distribution stress tensile generated during a mechanical test by the finite element method. Moreover, were made feldspathic ceramic discs, lithium disilicate discs and Y-TZP zirconia discs to analyze the influence of biaxial flexure stress of these three different techniques. These discs (veneer ceramic and zirconia ceramic) were joined following the three different techniques (conventional, Rapid Layer and CAD-on). They were also made FPDs 3 elements: following the same design of models used in finite element analysis. These crowns were cycled during 2x106 cycles to analyze failure at veneer ceramic, such as cracks, chipping, delamination and catastrophic failure. The results showed that the crowns made from ceramic lithium disilicate and low fusion glass ceramic at the interface veneer ceramic/infraestructure showed low concentration of tensile stress when compared to models made by the conventional technique, which showed a greater concentration of tensile stress between layers (veneer ceramic, interface and infrastructure). For the discs samples, the multilayer materials showed lower crack propagation between the ceramic layers. The cycled crowns showed no failure as cracks, chipping, delamination and catastrophic failure for the first 500,000 cycles. However, the prostheses made with feldspathic ceramic showed cracks from 1.106 cycles. The incorporation of functionally and aesthetically graded layers would be realisable, considerable research would be required before the feasibility of the conceptual approach could be accurately assessed. / FAPESP: 2012/11095-0
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/138191 |
| Date | 28 January 2016 |
| Creators | Costa, Anna Karina Figueiredo [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Borges, Alexandre Luiz Souto [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 600 |
Page generated in 0.0029 seconds