Specimens of steel 42CrMoS4 were quenched from the austenite (γ) and the ferrite (α) + austenite + cementite phase fields to produce fully martensitic matrices with 0 – 14 % ferrite dispersed in the matrix. After tempering at 300°C or 600°C mechanical and fatigue properties were determined. As expected yield strength, tensile strength and hardness decreased with increased tempering temperature and ferrite content. Quite unexpected, the fatigue properties were mildly affected. A small amount of ferrite, approximately 3% even appears to improve the fatigue strength. Then, at even higher ferrite amounts, slightly below 20% the fatigue strength appears to decrease again.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-102023 |
| Date | January 2012 |
| Creators | Hanno, Mithaq Elias |
| Publisher | KTH, Materialvetenskap |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds