CoordenaÃÃo de AperfeiÃoamento de NÃvel Superior / Este trabalho apresenta o estudo da sÃntese de nanopartÃculas de ferritas de nÃquel e de cobalto usando o mÃtodo sol-gel proteico. Inicialmente, Ã resgatado o mÃtodo do grÃfico de Williamson-Hall na anÃlise dos dados de difraÃÃo de raios X. Este mÃtodo permite calcular o tamanho mÃdio de partÃcula e a microdeformaÃÃo. Ferritas de nÃquel apresentaram tamanhos de partÃculas que crescem com o aumento da temperatura de calcinaÃÃo. NanopartÃculas de ferrita de nÃquel foram caracterizadas por espectroscopia MÃssbauer. As amostras calcinadas a 400 ÂC apresentaram comportamento superparamagnÃtico ao passo que aquelas calcinadas em temperaturas superiores apresentaram comportamento magnÃtico. As ferritas de cobalto foram caracterizadas usando difraÃÃo de raios X, espalhamento de raios X a baixo Ãngulo e medidas de magnetizaÃÃo. As ferritas de cobalto nÃo apresentaram comportamento superparamagnÃtico. Na sÃntese das ferritas de cobalto, alguns parÃmetros associados com o controle do processo foram estudados: temperatura de calcinaÃÃo, tempo de calcinaÃÃo, taxa de aquecimento/resfriamento. Deduziu-se a relaÃÃo de cada parÃmetro com o controle do tamanho de partÃcula e das propriedades das ferritas de cobalto. / In this work we present the study of the synthesis of nanosized nickel and cobalt ferrites by sol-gel proteic method. This work revisited the method of X-ray powder diffraction analysis known as Williamson-Hall plotting. This method provides size-strain studies in nanoparticles samples. Nickel ferrites has presented particle sizes that increase when the calcination temperature increases. Nickel ferrites nanoparticles were characterized by MÃssbauer spectroscopy. Sample calcined at 400ÂC has presented superparamagnetic properties and those calcined at higher temperatures behavior as magnetic materials.
Cobalt ferrites nanoparticles were charcterized by X-ray powder diffraction, small angle X-ray scattering e magnetization. Cobalt ferrites has not presented superparamagnetic behavior. For the synthesis of cobalt ferrites some parameters that are important to the process control were studied: calcination temperature, calcination time, heat rate. We have shown the relation among those parameters and the particle size and properties
control to the cobalt ferrite nanoparticles.
| Identifer | oai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:4887 |
| Date | 09 December 2011 |
| Creators | Nizomar de Sousa GonÃalves |
| Contributors | Jose Marcos Sasaki |
| Publisher | Universidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em FÃsica, UFC, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Unknown |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0031 seconds