2013_GuilhermeSiqueiraGomide.pdf: 2491036 bytes, checksum: 42a216e38bec945a3ef4b94838451101 (MD5) / Este trabalho apresenta um estudo da anisotropia e das propriedades
magnéticas intrínsecas e coletivas, realizado em nanopartículas de ferritas
mistas de Zn-Mn com diferentes teores de zinco. Essas propriedades foram
investigadas através da análise de diferentes técnicas de magnetização DC,
como: magnetização a baixo campo em função da temperatura, magnetização
em função do campo magnético aplicado a baixa temperatura, e gráficos do tipo
Henkel. Todas as medidas foram realizadas em um magnetômetro de amostra
vibrante (VSM-PPMS), em dois diferentes regimes de concentração, de modo a
investigar a interações entre partículas e suas influências sobre as propriedades
magnéticas dos sistemas estudados. As nanopartículas utilizadas possuem em
sua superfície uma camada de maguemita, a fim de permitir a formação de um
ferrofluido estável em meio ácido. As partículas são, portanto, consideradas do
tipo core-shell, denotadas por ZnxMn(1-x)Fe2O4@γ-Fe2O3, onde x é teor de zinco
e assume diversos valores. A variação da anisotropia nas diferentes amostras
foi investigada a partir da alteração na temperatura de bloqueio de Néel, e
também através de ciclos de histerese a baixas temperaturas, analisadas
utilizando a teoria de Stoner-Wohlfarth. Finalmente, a fim de observar os efeitos
das interações entre partículas em amostras de baixa anisotropia magnética, as
diferentes formas de aquisição da remanência e as relações entre elas,
denominadas relações de Wohlfarth foram estudadas. A não concordância dos
dados experimentais com tais relações permitiu verificar o efeito da distância
entre as partículas nas propriedades magnéticas, através da comparação entre
os dois regimes de concentração estudados. ______________________________________________________________________________ ABSTRACT / This work presents a study of the anisotropy and intrinsic and collective
magnetic properties, carried out on nanoparticles of mixed Zn-Mn ferrites with
different zinc content. These properties were investigated through the analysis of
different DC magnetization techniques, such as magnetization as a function of
temperature at low field, magnetization as a function of the applied magnetic field
at low temperatures and Henkel plots. All the measurements were carried out in
a vibrating sample magnetometer (VSM – PPMS), in two different concentration
regimes, in order to investigate the interaction between particles end it’s influence
over the magnetic properties of the studied systems. The nanoparticles utilized
have in it’s surface a layer of maghemite, in order to allow the formation of a
stable ferrofluid in acidic medium. The nanoparticles are, then, considered of the
core-shell type, and can be denoted by ZnxMn(1-x)Fe2O4@γ-Fe2O3, where x is the
zinc content, that can assume several values. The variation of the magnetic
anisotropy throughout the different samples was investigated through the change
in the Néel blocking temperature, also, through hysteresis cycles under low
temperatures, analyzed using the Stoner-Wohlfarth theory. Finally, with the intent
of observing the effects of the interparticle interactions in samples with small
magnetic anisotropy, the different ways of acquiring the remanence and the
relations between them, referred to as the Wohlfarth relations, were studied. The
discordance between the experimental data and those relations allowed for a
verification of the effect of the interparticle distance on the magnetic properties,
through the comparison between the two studied concentration regimes.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/14722 |
Date | 27 August 2013 |
Creators | Gomide, Guilherme Siqueira |
Contributors | Depeyrot, Jérôme |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB |
Rights | A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data., info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds