Laboratory experiments were conducted to observe, document and evaluate the mechanical behavior of Fiber Reinforced Concrete after being submitted to five different environments for 8 months. The specimens were molded and reinforced with synthetic fibers with a composition similar to that used for dry-cast concrete. Four different types of fibers with different composition were used. The fibers were mixed with the concrete to create the samples and the samples were exposed to different environmental conditions. Some of these environments were meant to increase degradation of the interface fiber-concrete to simulate longevity and imitate harsh environments or marine conditions. The environments consisted of: a high humidity locker (laboratory conditions), submerged in the Intracoastal Waterway in a barge (SeaTech), a wet/dry cycle in seawater immersion simulating a splash/tidal zone, low pH wet/dry seawater immersion cycle and samples submerged in calcium hydroxide solution. The latter three were in an elevated temperature tank (87-95°F) to increase degradation process. The specimens were monitored weekly and the environments were controlled. Then, specimens were evaluated using different mechanical testing as the Indirect Tensile (IDT) test method, compressive strength according to ASTM standards. Results of testing were documented and observed in this study for further understanding of mechanical properties of Fiber Reinforced concrete. Forensic observation of fiber distribution after the IDT tests were also performed. / Includes bibliography. / Thesis (M.S.)--Florida Atlantic University, 2019. / FAU Electronic Theses and Dissertations Collection
Identifer | oai:union.ndltd.org:fau.edu/oai:fau.digital.flvc.org:fau_41398 |
Contributors | Santillan Barragan, Ingrid Susana (author), Presuel-Moreno, Francisco (Thesis advisor), Florida Atlantic University (Degree grantor), College of Engineering and Computer Science, Department of Ocean and Mechanical Engineering |
Publisher | Florida Atlantic University |
Source Sets | Florida Atlantic University |
Language | English |
Detected Language | English |
Type | Electronic Thesis or Dissertation, Text |
Format | 79 p., application/pdf |
Rights | Copyright © is held by the author with permission granted to Florida Atlantic University to digitize, archive and distribute this item for non-profit research and educational purposes. Any reuse of this item in excess of fair use or other copyright exemptions requires permission of the copyright holder., http://rightsstatements.org/vocab/InC/1.0/ |
Page generated in 0.0124 seconds