Investigação do crescimento de fibras monocristalinas de LiLa(WO4)2 codopadas com Yb3+ e Er3+ para estudos espectroscópicos / Growth study of Yb3+ and Er3+-doped LiLa(WO4)2 single crystal fibers for spectroscopic characterization

Neste trabalho foi estudado o crescimento de fibras da matriz LiLa(WO4)2 (LLW) pura e co-dopada com íons Yb3+ e Er3+ via micro pulling-down. Foram crescidas fibras homogêneas e transparentes de LiLa(WO4)2:Yb3+:Er3+ com teor de dopante de 2, 5, 7, 10 e 15 mol% de Yb3+, todas co-dopadas com teor de 0,5 mol% de Er3+, com 1mm de diâmetro e até 22 mm de comprimento. Partindo-se da dopagem de 20 mol% não foi possível o crescimento de fibras com a mesma qualidade das demais, ocorrendo segregação e, possivelmente, formação de fase secundária. A temperatura de fusão dos compostos diminui com a adição de Yb3+, indo de 1020°C para o LLW puro, para 991°C com dopagem de 20 mol%. Para a análise de espectroscopia de emissão, as fibras foram excitadas com laser na região do infravermelho em 972 nm, sendo observada a emissão dos íons Er3+ via conversão ascendente. Foram observadas emissões referentes às transições 4S3/2 → 4I15/2 (centroide em 550 nm), 2H11/2 → 4I15/2 (527 nm) e 4F9/2 → 4I15/2 (653 nm); sendo a primeira a mais intensa. A eficiência de emissão aumentou de ~7% para a fibra pura, para 36% na fibra com 15 mol% de Yb3+. Foi encontrado que, para a maior intensidade de emissão, a quantidade ideal de Yb3+ deve ser de 11,5 mol%. / In the current work, was studied the growth of pure and Yb3+ and Er3+-doped LiLa(WO4)2 (LLW) by micro pulling-down technique. Were grown homogeneous and transparent fibers of Yb3+:Er3+:LiLa(WO4)2 with a dopant content of 2, 5, 7, 10 and 15 mol% of Yb3+, all co-doped with 0.5 mol% Er3+, 1 mm diameter and up to 22 mm length. It was not possible grow fibers with 20 mol% of Yb3+ due segregation and, possibly, formation of secondary phases. Noticed the melting temperature of the doped compounds decreases with the addition of Yb3+, from 1020 °C (pure LLW) to 991 °C (20 mol% Yb-doped). For emission studies, the fibers were excited in the infrared region at 972 nm and up conversion emission of Er3+ ions was registered. Emissions referring to transitions 4S3/2 → 4I15/2 (centroid at 550 nm), 2H11/2 → 4I15/2 (527 nm) and 4F9/2 → 4I15/2 (653 nm) were observed; the first one being the most intense. Emission efficiency increased from ~ 7% in pure fiber to 36% in doped fiber with 15 mol% of Yb3+. It was found that, for the highest emission intensity, the ideal amount of Yb3+ should be 11.5 mol%.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-21082018-150358
Date21 June 2018
CreatorsDenaldi, Rafael Lima
ContributorsBaldochi, Sonia Licia
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguagePortuguese
TypeDissertação de Mestrado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.0018 seconds