Flexural strength and marginal fit of two types of lithium disilicate ceramics for crowns

OBJECTIVES: To evaluate the flexural strength of 5 ceramic dental materials and to compare the marginal fit of crowns made with e.max press and a new experimental (EXP) press ceramic.
MATERIALS AND METHODS: The materials tested for flexural strength included: E.max press, E.maxCAD, ENAMIC, Experimental press, and Experimental-CAD. Each group (N= 10) was tested using the Instron 5566A using the piston-on-three-balls test.
For the crown fit experiment an Ivorine tooth was prepared with a chamfer finish and used as the master die. Wax up crowns were made on the die and pressed with E.max press and the Experimental press. 5 crowns per material were obtained. A similar procedure was used with standard aluminum crown dies. Copings were waxed up and pressed: 3 copings of E.max and 6 copings of EXP. Eight measurements of marginal fit per restoration were obtained with an optical microscope at 200×.
The data was analyzed using ANOVA and a post hoc Tukey-HSD test (Significance level = 0.05).
RESULTS: Mean and SD Flexural Strength values (MPa) per group were: E.max press: 486.96 (30.42). EXP press 378.16 (88.13). E.maxCAD 493.28 (55.2). EXP-CAD 420.63 (86.05). ENAMIC 157.59 (6.27).
Mean and SD values for margin fit per group (Microns) were: E.max press 74 (19). EXP press 65 (19).
CONCLUSIONS: E.max press has 28.8% higher FS than EXP press (P=0.0044).
ENAMIC had the lower FS (as expected).
EXP press had significantly lower marginal gap than E.max press by 12.2%. / 2018-09-28T00:00:00Z

Identiferoai:union.ndltd.org:bu.edu/oai:open.bu.edu:2144/18731
Date28 September 2016
CreatorsMunguia, Gerardo
Source SetsBoston University
Languageen_US
Detected LanguageEnglish
TypeThesis/Dissertation

Page generated in 0.0021 seconds