Böjhållfasthet på litiumdisilikatbaserad glaskeram beroende på termocyklingstid / Flexural strength on lithium disilicate based glass ceramic depending on thermal cycling time

Syfte Syftet med föreliggande studie var att undersöka böjhållfastheten hos IPS e.max CAD före och efter termocykling med 10 000 respektive 15 000 cykler. Material och metod Trettio provkroppar framställdes från fem stycken IPS e.max CAD LT-block. Provkropparna var indelade i två testgrupper (GT10 och GT15), och en kontrollgrupp (GK), á 10 provkroppar i varje. Provkropparna utformades enligt måtten L 17,9 ± 0,03 mm x B 2,5 ± 0,03 mm x H 2,5 ± 0,03 mm. Samtliga provkroppar kristalliserades och grupp GK förvarades i rumstemperatur, resterande två grupper, GT10 och GT15 termocyklades i 10 000 respektive 15 000 cykler.Därefter utfördes ett trepunkts böjhållfasthetstest. Resultaten analyserades med One-way ANOVA, Tukey’s test med signifikansnivån α= 0,05 i statistikprogrammet SPSS. Resultat Resultaten visade att det inte fanns någon signifikant skillnad mellan grupp GK och GT10 (p>0,05) respektive mellan grupp GT10 och GT15 (p>0,05). Grupp GT15 hade högst medelvärde (516 MPa) och grupp GK hade lägst medelvärde (450 MPa). Signifikant skillnad fanns mellan grupp GK och GT15 (p<0,05). Grupp GT15 hade en signifikant högre böjhållfasthet (~470-637 MPa) jämfört med grupp GK (~406-494 MPa). Slutsats Inom föreliggande studies begränsningar kan följande slutsatser dras: Termocykling med 10 000 cykler påverkar inte böjhållfastheten, däremot ger ökat antal cykler (15 000) högre böjhållfasthet. / Purpose  The purpose of the present study was to investigate the flexural strength of IPS e.max CAD beforeand after thermal cycling with 10,000 and 15,000 cycles, respectively.  Material and method  Thirty specimens were prepared from five IPS e.max CAD LT blocks, divided into two test groups (GT10 and GT15), and one control group (group GK) (n=10). The specimens were designed with the dimensions L 17.9 ± 0,03 mm x W 2.5 ± 0,03 mm x H 2.5 ± 0,03 mm. All specimens were crystallized and group GK was kept in room temperature, the remaining two groups, GT10 and GT15 were thermocycled with 10,000 and 15,000 cycles respectively. A three-point flexural strength test was performed. The results were analyzed with One-way ANOVA, Tukey's test with a significance level α = 0.05 in the statistical program SPSS.  Results  The results showed that there was no significant difference between groups GK and GT10 (p> 0.05), and between groups GT10 and GT15 (p> 0.05). It was also observed that group GT15 had the highest average (516 MPa) and group GK had the lowest average (450 MPa). There was a significant difference between groups GK and GT15 (p <0.05). Group GT15 had a significantly higher flexural strength (~ 470-637 MPa) compared to group GK (~406-494 MPa).  Conclusion  Within the limitations of the present study, the following conclusions can be drawn:Thermal cycling comprising 10,000 cycles do not affect the flexural strength, however, increasing the number of cycles (15,000) will give higher flexural strength.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:mau-52436
Date January 2022
CreatorsZheng, Yi
PublisherMalmö universitet, Odontologiska fakulteten (OD)
Source SetsDiVA Archive at Upsalla University
LanguageSwedish
Detected LanguageEnglish
TypeStudent thesis, info:eu-repo/semantics/bachelorThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.002 seconds