This thesis investigates using friction stir welding to repair common surface defects found in aluminum-silicon sand castings. Wherein, the effect of welding parameters: weld RPM, weld speed, and number of weld passes, were evaluated using hardness, porosity density, welding temperature, microstructure refinement as metrics. Therefrom, the results strongly suggest friction stir welding: reduces porosity size, reduces porosity density in a specific area, increases average hardness, improves hardness uniformity, increases surface roughness, redistributes microstructure features in a manner that theoretically improves strength, and maintains a welding temperature less than 660 degrees Celsius.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:hv-16675 |
| Date | January 2021 |
| Creators | Bates, William |
| Publisher | Högskolan Väst, Avdelningen för Industriell ekonomi, Elektro- och Maskinteknik |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds