Previous issue date: 1999 / Resumo: Considerando as dificuldades técnicas existentes na confecção de restaurações fundidas, onde o mínimo desajuste acarreta sérios problemas clínicos futuros, este trabalho visou analisar o ajuste cervical e interno de coroas totais metálicas sem e com alívio interno (espaçador de troquei, ataque químico com ácido nítrico e jateamento com partículas de óxido de alumínio), confeccionadas com liga de
paládio/prata (Pors-on 4), com três diferentes tipos de término cervical: ombro reto, ombro biselado em 20° e chanfro reto em 45°. Para fusão da liga foram utilizadas duas fontes de calor de fundição: gás-oxigênio e resistência elétrica. Após a fundição, as coroas foram assentadas sobre seus respectivos troquéis, sob carga estática de 9 kg. As leituras do desajuste cervical e da interface troquei-coroa das secções transversais foram realizadas em microscópio metrológico (Carl Zeiss), provido de um relógio comparador digital, série 543 IDF (Mitutoyo). Os resultados foram submetidos à análise de variância e ao teste de Tukey (5%) e demonstraram que: os melhores ajustes cervical e interno foram obtidos com a fonte de calor de fundição gás-oxigênio; independente de todos fatores analisados, o término cervical em chanfro reto de 45° apresentou os melhores ajustes, tanto cervical como interno; e, o melhor alívio interno foi o realizado na pós-fundição com jateamento com óxido de alumínio / Abstract: Regarding the existenting difficulties in making casting restorations, where the minimal cervical discrepancy lead to a future serious clinical problems, this research will analyse the cervical and internal fits of total metal crowns with or not internal relief (die-spacing, acid conditioning and sandblaster with aluminiun oxide), making with palladium-silver alloy (Pors-on 4), with three different marginal configurations: shoulder, 20-degree bevel shoulder and 45-degree chamfered, on the stainless steel dies. To cast the alloys, two heat sources have been used: gas-oxygen and eletric resistance. After the casting, the specimens were seated on the dies, with a static load of 9 kg. The reading of the cervical fit and die/crown interface was made on a metric microscope (Carl Zeiss), using a digital micrometer (Mitutoyo). The results were submitted to analysis of variance and Tukey's test (5%), indicated that the better cervical and internal fits were obtained with the heat source gas-oxigen; the marginal configuration 45-degree
chamfer showed the highest fit cervical and internal; and, the better internal relief was sandblaster with aluminium oxide / Doutorado / Doutor em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290092 |
| Date | 11 December 1999 |
| Creators | Milan, Fabio Machado |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Simonides, 1939-, Ono, Rosana, Boscarioli, Ana Paula, Goes, Mario Fernando de, Sinhoreti, Mário Alexandre Coelho |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 141p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.003 seconds