Previous issue date: 2003 / Resumo: Apresentamos, neste trabalho, um estudo da dopagem residual e intencional, do ordenamento e das interfaces no crescimento epitaxial de InGaP/GaAs com os parâmetro de rede casados. O objetivo do trabalho é propiciar a obtenção de dispositivos com este material.
Para a dopagem residual verificamos que o Carbono é o principal dopante. Sua incorporação ocorre, ao mesmo tempo, tanto como doador quanto como aceitador. A proporção entre a parte doadora e aceitadora depende da temperatura de crescimento.
Para as dopagens com o Silício, verificamos, em baixas temperaturas de crescimento e concentrações de Si menores que aproximadamente 4,0x10 18 cm -3, que a concentração de portadores é proporcional à pressão de vapor deste elemento na célula de efusão do Si. Vimos que para maiores temperaturas de crescimento ocorre um aumento da concentração de portadores e a cristalinidade do material melhora.
Para as dopagens com o Berílio, verificamos, em altas temperaturas de crescimento e concentrações de Be menores que aproximadamente 3,0x10 18 cm -3 , que a concentração de portadores é proporcional à pressão de vapor deste elemento na célula de efusão do Be. Observamos que para menores temperaturas de crescimento ocorre um aumento da concentração de portadores e a cristalinidade do material melhora.
Tanto no caso do Si como no do Be, a análise dos resultados indica a formação de complexos Si-C e Be-P, respectivamente.
Dentro da faixa de temperatura estudada (500oC - 580oC), verificamos que o ordenamento no InGaP aumenta linearmente com o aumento da temperatura de crescimento e que a razão V/III influencia levemente o ordenamento. Para altas temperaturas de crescimento observamos uma relação entre as estruturas superficiais e as regiões ordenadas.
Realizamos também crescimentos de poços quânticos de InGaP/GaAs/InGaP, para o estudo de suas interfaces. Identificamos a formação de uma camada de InGaAsP na interface InGaP-GaAs. Através do estudo dos parâmetros de crescimento conseguimos minimizar a formação desta camada e aumentar a qualidade das interfaces.
Por fim, mostramos a aplicação do nosso estudo em dispositivos / Abstract: In this work we present a study on residual and intentional dopant elements, on ordering and on interfaces of InGaP lattice matched with GaAs. The goal of this study is to obtain semiconductor devices using this material.
We have found that Carbon is the main residual dopant. It is incorporated as donor and as acceptor, the ratio between these two incorporation modes depends on the growth temperature.
For intentional silicon doping, it was found that, at low growth temperatures and Si concentration lower than 4,0 x10 18 cm -3 , silicon incorporation as donor is proportional to the Si vapour pressure in the Si effusion cell temperature. For higher growth temperatures, Si-donor concentration increases and there is an improvement on crystal quality.
For intentional Beryllium doping, it was found that, at high growth temperatures and Be concentration lower than 3,0 x10 18 cm -3 , beryllium as acceptor incorporation is proportional to the Be vapour pressure in the Be effusion cell. For lower growth temperatures, Be-acceptor concentration increases and there is an improvement on crystal quality.
In Si as well as in Be dopage, the data analysis indicates the complex formation of Si-C and Be-P, respectively .
In the usual growth temperature range (500oC - 560oC) we have also verified that the ordering increases as the temperature increases and it is almost insensitive to the III/V ratio. For higher growth temperatures, we have found a relationship between surface structures and ordered regions.
In growing InGaP/GaAs/InGaP quantum wells, we have found an InGaAsP layer formation at the interface InGaP/GaAs. We were able to minimize this layer and improve the interface quality.
Finally, we could show the application of our study in some semiconductor devices / Doutorado / Física / Doutor em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/278399 |
| Date | 03 August 2018 |
| Creators | Bettini, Jefferson |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Carvalho, Mauro Monteiro Garcia de, 1948-, Cotta, Mônica Alonso, Ugarte, Daniel Mário, Leite, Jose Roberto, Cardoso, Lisandro Pavie |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Física Gleb Wataghin, Programa de Pós-Graduação em Física |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 139p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0016 seconds