This thesis work is focused on the influence of process parameters during gas atomization on the thermal spraying properties of a Ni-Cr-B-Si hardfacing alloy. The metal powder alloy, known as 1-60-20, is produced by Höganäs AB. There have been problems with insufficient fusing during flame spraying of this particular alloy sometimes, even though the chemical composition is always within spec. This has lead to a theory that the difference in performance is caused by differences in parameters during gas atomization. Several gas-gas and gas-water atomizations with varying parameters were performed at the Höganäs Pilot Centre. The powder samples were then analyzed by sieving, scanning electron microscopy, x-ray diffraction and finally tested by powder welding. The results show that by increasing the cooling rate during gas atomization the formation of unstable Ni-borides is possible for this alloy. If these Ni-borides will enhance the fusing properties of the alloy is unknown. According to the literature studied, it should however improve the fusing properties.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-180352 |
| Date | January 2015 |
| Creators | Pettersson, Tim |
| Publisher | KTH, Materialvetenskap |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0039 seconds