Microstructural features at different scales affect the constitutive stress-strain response and the fatigue crack initiation life in Ni-base superalloys. While numerous efforts have been made in the past to experimentally characterize the effects of these features on the stress-strain response and/or the crack initiation life, there is a significant variability in the data with sometimes contradictory conclusions, in addition to the substantial costs involved in experimental testing. Computational techniques can be useful tools to better understand these effects since they are relatively inexpensive and are not restricted by the limitations in processing techniques.
The effect of microstructure on the stress-strain response and the variability in fatigue life were analyzed using two Ni-base superalloys; DS GTD111 which is a directionally solidified Ni-base superalloy, and IN100 which is a polycrystalline Ni-base superalloy. Physically-based constitutive models were formulated and implemented as user material subroutines in ABAQUS using the single crystal plasticity framework which can predict the material stress-strain response with the microstructure-dependence embedded into them. The model parameters were calibrated using experimental cyclic stress-strain histories. A computational exercise was employed to quantify the influence of idealized microstructural variables on the fatigue crack initiation life. Understanding was sought regarding the most significant microstructure features using explicit modeling of the microstructure with the aim to predict the variability in fatigue crack initiation life and to guide material design for fatigue resistant microstructures. Lastly, it is noted that crystal plasticity models are often too computationally intensive if the objective is to model the macroscopic behavior of a textured or randomly oriented 3-D polycrystal in an engineering component. Homogenized constitutive models were formulated and implemented as user material subroutines in ABAQUS, which can capture the macroscale stress-strain response in both DS GTD111 and IN100. Even though the study was conducted on two specific Ni-base superalloys; DS GTD111 and IN100, the objective was to develop generic frameworks which should also be applicable to other alloy systems.
| Identifer | oai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/11515 |
| Date | 01 June 2006 |
| Creators | Shenoy, Mahesh M. |
| Publisher | Georgia Institute of Technology |
| Source Sets | Georgia Tech Electronic Thesis and Dissertation Archive |
| Language | en_US |
| Detected Language | English |
| Type | Dissertation |
| Format | 8718311 bytes, application/pdf |
Page generated in 0.0017 seconds