Growth and Applications of Periodically Poled Lithium Niobate Crystal Fibers

¡@¡@We integrated the laser-heated pedestal growth (LHPG) system with accurately controlled electrodes to build up our in situ poling system. The ZnO and MgO doped periodically poled lithium niobate crystal fiber were fabricated with the poling system. This poling system has the advantage of convenience and fast growth, but the ¡§screen effect¡¨ caused by free charges which exist near the molten zone must be eliminated. The micro swing resulted from the electric force is a feasible solution, because it can disarrange the free charges and reduce the ¡§screen effect¡¨. However, without excellently controlled micro swing, the uniformity of the poled domain pitch will loose and the conversion efficiency can not be improved. After analysis of the measured current data, the approximate system current model was presented and the proportional dependence between system current and micro swing was verified. Thus the system current was applied as the micro swing feedback signal, with that the variation of the micro swing was reduced from 25% to 15%. The stability of CO2 laser power is also a dominant factor to determine the quality of poled crystal fiber. The variation of the CO2 laser power was controlled within 1%. All the complicated works and precise control during the crystal fiber growth were accomplished with the LabVIEW program.
¡@¡@A novel and simple self-cascaded SHG + SFG scheme is presented for the generation of tunable blue/green light using ZnO doped periodically poled lithium niobate crystal fiber (PPLNCF) with a single designed pitch. A PPLNCF with a uniform period of 15.45£gm, the maximum conversion efficiency for the second harmonic generation and the cascaded SHG + SFG blue light can reach up to -9.2 dB and -31.9 dB, respectively. The 3 dB bandwidth of the tunable blue light is 3 nm (475-478 nm). In order to expand the tuning bandwidth range, a QPM gradient periodical structure was designed and can provide a 3 dB bandwidth of 65 nm for the tunable blue/green light output by simulation. We have successfully grown a crystal fiber with the domain pitch of 18.9 £gm for the C-band wavelength converter. The crystal length is 1.8 mm, the effective nonlinear coefficient of the lithium niobate crystal fiber is 18.2 pm/V that equals 0.53¡Ñdideal (34.4 pm/V). The conversion efficiency for converting the CW laser in C-band is about -59.3 dB.

Identiferoai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0907110-093815
Date07 September 2010
CreatorsLee, Li-Min
ContributorsSheng ¡VLung Huang, Wood-Hi Cheng, Yen-Sheng Lin, Yi-Jen Chiu, Hung-Wen Chang
PublisherNSYSU
Source SetsNSYSU Electronic Thesis and Dissertation Archive
LanguageEnglish
Detected LanguageEnglish
Typetext
Formatapplication/pdf
Sourcehttp://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0907110-093815
Rightsoff_campus_withheld, Copyright information available at source archive

Page generated in 0.0023 seconds