The increased use of thermoplastics in load carrying components, especially in the automotive industry, drives the needs for a better understanding of its complex mechanical properties. In this thesis work for a master degree in solid mechanics, the mechanical properties of a PA 6/66 resin with and without reinforcement of glass fibers experimentally been investigated. Topics of interest have been the dependency of fiber orientation, residual strains at unloading and compression relative tension properties. The experimental investigation was followed by simulations implementing existing and available constitutive models in the commercial finite element code LS-DYNA. The experimental findings showed that the orientation of the fibers significantly affects the mechanical properties. The ultimate tensile strength differed approximately 50% between along and cross flow direction and the cross-flow properties are closer to the ones of the unfilled resin, i.e. the matrix material. An elastic-plastic model with Hill’s yield criterion was used to capture the anisotropy in a simulation of the tensile test. Residual strains were measured during strain recovery from different load levels and the experimental findings were implemented in an elastic-plastic damage model to predict the permanent strains after unloading. Compression tests showed that a stiffer response is obtained for strains above 3% in comparison to tension. The increased stiffness in compression is although too small to significantly influence a simulation of a 3 point bend test using a material model dependent of the hydrostatic stress.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-103790 |
| Date | January 2012 |
| Creators | Appelsved, Peter |
| Publisher | KTH, Hållfasthetslära (Inst.) |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0089 seconds