With the discovery of conductivity in doped polyacetylene (PA), a new era in synthetic metals has emerged by breaking the traditionally accepted view that polymers were always insulating. Conducting polymers are essentially characterized by the presence of conjugated bonding on the polymeric back bone, which facilitates the formation of polarons and bipolarons as charge carriers. Among the numerous conducting polymers synthesized to date, polypyrrole (PPy) is by far the most extensively studied because of prodigious number of applications owing to its facile polymerizability, environmental stability, high electrical conductivity, biocompatibility, and redox state dependent physico-chemical properties. Electrochemically prepared PPy is more interesting than the chemically prepared polymer because it adheres to the electrode surface and can be directly used for applications such as supercapacitors, electrochemical sensors, electromechanical actuators and drug delivery systems.
In quest for improvement in quality of the device performances in the mentioned applications, micro and nano structured polymeric materials which bring in large surface area are studied. Finding a simple and efficient method of synthesis is very important for producing devices of PPy microstructures. Till date, Hard and soft template methods are the most employed methods for synthesis of these structures. Soft template based electrochemical methods are better than hard template methods to grow clean PPy microstructures on electrode substrates as procedures for removal of hard templates after the growth of microstructures are very complex. As per the literature, there is no unique method available to grow PPy microstructures which can demonstrate several applications. Although gas bubble based soft template methods are exploited to grow conducting polymer microstructures of sizes in few hundreds of micrometers, studies on applications of the same are limited. Hence it is planned to develop procedures to grow microstructures that can be used in several applications. In the current work, PPy microstructures with high coverage densities are synthesized on various electrode substrates by soft template based electrochemical techniques.
Hollow, hemispherical and spherical PPy microstructures are developed by a two step method using electro generated hydrogen bubble templates on SS 304 electrodes. In the first step, Hydrogen bubbles are electro generated and stabilized on the electrode in the presence of β- naphthalene sulfonic acid (β-NSA). In the second step, Pyrrole is oxidised over the bubble template to form PPy microstructures. Microstructures (open and closed cups) of average size 15 μm are uniformly spread on the surface with a coverage density of 2.5×105 units /cm2.
Globular PPy microstructures are developed by a single step method using concomitantly electro generated oxygen bubble templates on SS 304 electrodes during electropolymerization. Microstructures of average size 4 μm are uniformly spread on the surface with a coverage density of 7×105 units/cm2.
Surfactant properties of Zwitterionic 4-(2-hydroxyethyl)-1-piperazine ethane sulfonic acid (HEPES) are exploited for the first time to grow conducting polymer microstructures. Ramekin shaped PPy microstructures are developed using HEPES as the surfactant to stabilize hydrogen bubble templates in a two step electrochemical synthesis method. Microramekins of size 100 µm are uniformly spread on the surface with a coverage density of 3000 units/cm2. Micropipettes and microhorns of PPy are synthesised by a single step electrochemical route using HEPES as a surfactant. Hollow micropipettes of length 7 µm with an opening of 200 nm at the top of the structure are observed. Similarly microhorn/celia structures are observed with length 10-15 µm. Microcelia are uniformly distributed over the surface with each structure having a diameter of 2 µm at the base to 150 nm at the tip. Growth mechanism based on contact angle of the reactant solution droplets on the substrate is proposed.
PPy microstructures are characterized by scanning electron microscopy, X-Ray photoelectron spectroscopy, Fourier transform infrared spectroscopy, Raman Spectroscopy and UV-Visible spectroscopy to study morphology, ‘chemical bonding and structure’ , ‘defects and charge carriers’.
Applicability of the electrodes with PPy microstructures in supercapacitors is investigated by cyclic voltammetry, chronopotentiometry and electrical impedance spectroscopy. Electrodes developed by all the above methods demonstrated very good supercapacitance properties. Supercapacitor studies revealed very high specific capacitances (580, 915, 728 and 922 F/g,) and specific powers (20, 25, 13.89 and 15.91 kW/kg) for electrodes with PPy microstructures (H2 bubble based two step method, O2 bubble based single step method, HEPES stabilized H2 bubbble method and HEPES based microhorn/celia structures respectively). Supercapacitive behavior of all the electrodes is retained even after an extended charge-discharge cycling in excess of 1500 cycles.
Horseradish peroxidase entrapped, bowl shaped PPy microstructures are developed for H2O2 biosensing. Amperometric biosensor has a performance comparable to the sensors reported in the literature with high sensitivity value of 12.8 μA/(cm2.mM) in the range 1.0 mM to 10 mM. Glucose oxidase entrapped PPy amperometric biosensor is developed for Glucose sensing. Sensitivity of 1.29 mA/(cm2.mM) is observed for β-D-Glucose sensing in the 0.1 mM to 5.0 mM range while 58 μA/(cm2.mM) is observed in the 5.0 to 40 mM range. Potentiometric urea sensor with urease entrapped PPy microstructures on SS electrode is developed. It is able to sense urea in the micromolar ranges down to 0.1 μM. It represented an excellent performance with sensitivity of 27 mV/decade. Sensitivity in the micromolar range is 4.9 mV/(μM.cm2).
Drug encapsulation and delivery is successfully demonstrated by two actuation means (i) by electrochemical actuation, (ii) by actuation based on pH changes. Concepts are proved by delivering a fluorescent dye into neutral and acidic solutions. Drug delivery is confirmed by UV-Visible spectroscopy and Fluorescence microscopy.
Finally, Micro/nanostructures with Tangerine, Hollow globular (Pani Poori), Chip, Flake, Rose, Worm, Horn and Celia shapes are synthesized electrochemically and scanning electron microscopic studies are presented. Controlled growth of microstructures on lithographically patterned gold interdigital electrodes is demonstrated with a future goal of creating addressable microstructures.
The studies reported in the thesis provide an insight on various applications of PPy microstructures (supercapacitors, sensors and drug delivery systems) developed by a unique methodology based on electrochemically generated gas bubble templates.
Identifer | oai:union.ndltd.org:IISc/oai:etd.ncsi.iisc.ernet.in:2005/2334 |
Date | 07 1900 |
Creators | Pavan Kumar, K |
Contributors | Nagaraju, J |
Source Sets | India Institute of Science |
Language | en_US |
Detected Language | English |
Type | Thesis |
Relation | G25307 |
Page generated in 0.0169 seconds