In polycrystalline silicon (pc-Si) thin-film solar cells, defect passivation is critical to device performance. Isoelectronic or covalently bonded impurities, hydrogenic, extended defects and defects with localized levels in the bandgap (deep level defects) are typically introduced during the fabrication of, and/or are inherent to, pc-Si thin-film solar cells. These defects dramatically affect minority carrier lifetimes. Removing and/or passivating these defects is required to maximize minority carrier lifetimes and is typically done through thermal annealing and passivation techniques. For pc-Si thin-film solar cells on low temperature glass superstrates, rapid thermal annealing (RTA) and hydrogen plasma passivation (hydrogenation) are powerful techniques to achieve effective removal and passivation of these defects. In this thesis, three silicon thin-film solar cells structures on low-temperature glass are subjected to variations in RTA high-temperature plateaus, RTA plateau times, and hydrogen plasma passivation parameters. These solar cells are referred to as ALICIA, EVA and PLASMA. By varying the RTA plateau temperature and time at plateau, the trade-off between extensive dopant diffusion and maximum defect removal is optimized. To reduce the density of point defects and to electrically activate the majority of dopants, an RTA process is shown to be essential. For all three of the thin-film solar cell structures investigated in this thesis, a shorter, higher-temperature RTA process provides the best open-circuit voltage (Voc). Extensive RTA plateau times cause excessive dopant smearing, increasing n = 2 recombination and shunt resistance losses. Hydrogenation is shown to be an essential step to achieve maximum device performance by `healing' the defects inherent to pc-Si thin-film solar cells. If the hydrogen concentration is about 1-2 times the density of oxygen in the cells as measured by secondary ion mass spectroscopy (SIMS), the cells seem to respond best to hydrogenation, with good resultant Voc and short-circuit for all cells investigated in this thesis. The effect of hydrogen passivation on the Voc is spectacular, typically increasing it by a factor of 2 to 3.5. Hydrogen de-bonding from repeated thermal treatments at increasing temperature provides a deeper understanding of what defects exist and the nature of the defects that limit the cell voltage. The variation in RTA and hydrogenation process parameters produces significant empirical insight into the effectiveness of RTA processes for point defect removal, dopant activation, point defect and grain boundary passivation, and impurity passivation. SIMS measurements are used to determine the impurities present in the cells' bulk and the amount of hydrogen available to passivate defects. From the results presented it appears that pc-Si thin-film solar cells on low-temperature glass are a promising, and potentially lower-cost, alternative to Si wafer based cells.
| Identifer | oai:union.ndltd.org:ADTP/257487 |
| Date | January 2007 |
| Creators | Terry, Mason L, Photovoltaic & Renewable Energy Engineering, UNSW |
| Publisher | Awarded by:University of New South Wales. Photovoltaic and Renewable Energy Engineering |
| Source Sets | Australiasian Digital Theses Program |
| Language | English |
| Detected Language | English |
| Rights | Copyright Mason L Terry, http://unsworks.unsw.edu.au/copyright |
Page generated in 0.0014 seconds