The research goal of this work was dedicated to improvement of the properties and enhancement of the application potential of commodity polymer based on polyolefins by choosing different synthesis routes to create new structures and materials. More precisely, the presented study explores different aspects of metallocene and post-metallocene catalyzed olefin polymerization leading to synthesis of novel copolymers and nanocomposites.
The first part of this thesis deals with controlled polymerization of α-olefins catalyzed by post-metallocenes.
Bis(phenoxyamine) zirconium complexes with [ONNO]-type ligands bearing cumyl (bPA-c) and 1-adamantyl (bPA-a) ortho-substituents were applied. For the polymerization catalyzed by bPA catalyst quasi-living kinetic character is proposed. The bPA catalyst was applied for synthesis of block copolymers by employing the strategy of sequential monomer addition. The blocky structure of the copolymer was successfully achieved and confirmed by NMR techniques. Moreover, the monomodal distribution of molar mass in SEC chromatogram confirmed the absence of homopolymers.
In the second part of the work new defined comb-like copolymers (CLC) having a poly(10-undecene-1-ol) (PUol) backbone and densely grafted poly(ε-caprolactone) (PCL) side chains are presented. These copolymers were synthesized in two steps by means of metallocene polymerization followed by ring opening polymerization. Copolymers with varied and adjustable graft length (PCL segments) were synthesized. It was proved that the melting and crystallization temperatures of the CLC correlate with the PCL side chain length, i.e. longer chains result in higher Tm and Tc,o values. The melting enthalpy was found to be asymptotically dependent on the length of PCL side chains. The bulk morphology of the comb-like copolymers is proposed to be lamellar as judged from the TEM micrographs.
The third part of the thesis is focused on the synthesis of polypropylene nanocomposites via in situ polymerization. Thereby, organomodified aluminumphosphate with kanemite-type layered structure (AlPO-kan) has been used as novel filler. Melt compounding composites were prepared for comparison purposes to evaluate the influence of in situ synthesis on the dispersion quality of the filler in polymer matrix. Melt compounding of neat AlPO-kan with PP did not lead to formation of nanocomposites. TEM images show macro-composites with the lamellar solid remaining agglomerated. On the contrary, in situ polymerization of propene yielded materials with exfoliated nanocomposite morphology. In XRD, diffractions of the AlPO-kan pilling of layers are not detectable. It can be concluded that the primary existing layers are delaminated. Very fine distribution of the filler in the polypropylene matrix has been impressively demonstrated by TEM.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa.de:bsz:14-qucosa-166518 |
| Date | 07 July 2015 |
| Creators | Zakrzewska, Sabina |
| Contributors | Technische Universität Dresden, Fakultät Mathematik und Naturwissenschaften, Prof. Dr. Brigitte Voit, Dr. Ulrich Schulze, Prof. Dr. Brigitte Voit, Prof. Dr. Michael Buchmeiser |
| Publisher | Saechsische Landesbibliothek- Staats- und Universitaetsbibliothek Dresden |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | doc-type:doctoralThesis |
| Format | application/pdf |
Page generated in 0.0039 seconds