Human bone tissue has an inherent hierarchical structure, which is integral to its material properties. It is primarily composed of a collagen fiber matrix that is mineralized with hydroxyapatite. A comprehensive understanding of bone and the linkages between structural and cellular organization is imperative to developing fundamental knowledge that can be applied to better our understanding of bone disease manifestations and its interaction with implant devices. Herein, this thesis investigated non-traditional methods for evaluating bone structure across the nano- and meso-length scales.
Firstly, due to the inhomogeneous organization of collagen fibrils and mineral platelets of bone ultrastructure, a suitable methodology for the investigation of both phases needed to be generated. In this work, focused ion beam (FIB) microscopy was employed to create site-specific scanning transmission electron microscopy (STEM) lift-outs of human osteonal bone that could be visualized with correlatively with STEM and small angle X-ray scattering (SAXS). Samples were successfully characterized using both techniques, and minimal visual damage was induced during data acquisition. This work is the first to demonstrate the potential for bone to be investigated correlatively using both STEM and SAXS.
Secondly, this work is the first to employ a dual-beam plasma FIB (PFIB) equipped with a scanning electron microscope (SEM), to investigate bone tissue across the mesoscale. This equipment enables large volume three-dimensional (3D) imaging at nanoscale resolution across larger mesoscale volumes. This thesis aimed to reduce ion beam-based artifacts, which presents as curtain-like features by adjusting the composition of protective capping layers. Subsequently, large volume tomograms of bone tissue were acquired, demonstrating the effectiveness of the PFIB to reveal mesoscale features including the cellular network of bone tissue.
Overall, this thesis has developed methods that allow for the application of advanced microscopy techniques to enhance the understanding of bone tissue across the nanoscale and mesoscale. / Thesis / Master of Applied Science (MASc) / Bone tissue has a unique structure that perplexes both biologists and materials scientists. The hierarchical structure of bone has garnered the interest of materials scientists since the body’s skeletal strength and toughness are governed by the nanoscale (millionth of centimetres) to macroscale (centimeters) organization of bone. In this work, the intricate organization of bone is investigated using advanced electron and ion beam microscopy techniques, which achieve high-resolution imaging of bone structure. Firstly, this work developed a sample preparation workflow to correlate electron and X-ray imaging of the same bone tissue. Secondly, this work was the first to apply serial-sectioning plasma focused ion beam tomography to human bone tissue to investigate its structure at high resolution across micron-sized volumes. Here, previously unexplored methodologies to image bone are demonstrated with the hopes of applying such techniques to investigate healthy and pathological bone tissue in the future.
| Identifer | oai:union.ndltd.org:mcmaster.ca/oai:macsphere.mcmaster.ca:11375/24664 |
| Date | January 2019 |
| Creators | Binkley, Dakota M. |
| Contributors | Grandfield, Kathryn, Materials Science and Engineering |
| Source Sets | McMaster University |
| Language | English |
| Detected Language | English |
| Type | Thesis |