Oxygen Transport Measured by Isotope Tracing through Solid Oxides

The following thesis demonstrates two isotope tracing experiments that measure oxygen transport through electrochemically polarized solid oxides. Cathode-symmetric ‘button’ cells with yttria stabilized zirconia(YSZ) electrolytes and either strontium doped lanthanum manganate(LSM) or composite LSM/YSZ cathodes were studied. The first experiment measured the residence time distributions(RTD) of 34O2. The measured RTDs were compared at different temperatures(700-800°C) and applied potentials(-2 to -8V). Comparisons with simulated RTDs revealed that oxygen transport was laterally heterogeneous. Delamination of the counter electrode is likely the source of the heterogeneity. The second experiment measured a wave of 18O by exposing an interior cross section and applying ToF-SIMS analysis. A depth profile was produced that spans the cathode and electrolyte interface. The depth profile was compared with a variety of limiting oxygen activation scenarios predicted by a simple 1-D model. Comparisons demonstrated that oxygen activation is likely not restricted to the cathode and electrolyte interface.

Identiferoai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:OTU.1807/27372
Date31 May 2011
CreatorsWood, Thomas
ContributorsMims, Charles A.
Source SetsLibrary and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada
Languageen_ca
Detected LanguageEnglish
TypeThesis

Page generated in 0.002 seconds