Two industrial studies and one set of lab scale trials have been done. In addition, a theoretical study has been done. The main focus has been on non metallic inclusion composition during the ladle refining operation in industrial steel production. Sampling has been done together with careful inclusion determination. The inclusion composition is related to different variables. In the industrial trials samples have been taken at different steps during the ladle refining period. Steel and slag composition as well as temperature and oxygen activity have been determined. The thesis is based on five supplements with different major objectives, all related to the inclusion composition. The equilibrium top slag-steel bulk and inclusions-steel bulk were investigated by comparison between calculated and measured oxygen activity values. The oxygen activity and relation to temperature has also been discussed as well as oxygen activity and temperature gradients. The effect of vacuum pressure on inclusion composition has been evaluated in a theoretical study as well as lab scale trials. The inclusion composition has been studied during the industrial ladle treatment process. The inclusion composition was related to top slag composition and other parameters during ladle treatment. The major findings in the thesis are the lack of equilibrium conditions with respect to top-slag and steel bulk before vacuum treatment. The inclusions have been found to be closer to equilibrium with the steel bulk. Al/Al2O3 equilibrium has been found to control the oxygen activity after Al-deoxidation. Evaluation of inclusion composition during the ladle refining has revealed that the majority of the inclusions showed a continuous composition change throughout the ladle refining process, from high Al2O3, via MgO-spinel to finally complex types rich in CaO and Al2O3. The final inclusion composition after vacuum treatment was found to be close to the top slag composition. Vacuum pressure has been found to have a theoretical effect on inclusion composition at very low pressures. / QC 20100712
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-4673 |
| Date | January 2008 |
| Creators | Björklund, Johan |
| Publisher | KTH, Tillämpad processmetallurgi, Stockholm : KTH |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds