Heterojunction bipolar transistors and ultraviolet-light-emitting diodes based in the III-nitride material system grown by metalorganic chemical vapor deposition

The material and device characteristics of InGaN/GaN heterojunction bipolar transistors (HBTs) grown by metalorganic chemical vapor deposition are examined. Two structures grown on sapphire with different p-InxGa1-xN base-region compositions, xIn = 0.03 and 0.05, are presented in a comparative study. In a second experiment, NpN-GaN/InGaN/GaN HBTs are grown and fabricated on free-standing GaN (FS-GaN) and sapphire substrates to investigate the effect of dislocations on III-nitride HBT epitaxial structures. The performance characteristics of HBTs on FS-GaN with a 20×20 m2 emitter area exhibit a maximum collector-current density of ~12.3 kA/cm2, a D.C. current gain of ~90, and a maximum differential gain of ~120 without surface passivation. For the development of deep-ultraviolet optoelectronics, several various structures of optically-pumped lasers at 257, 246, and 243 nm are demonstrated on (0001) AlN substrates. The threshold-power density at room temperature was reduced to as low as 297 kW/cm2. The dominating polarization was measured to be transverse electric in all cases. InAlN material was developed to provide lattice matched, high-bandgap energy cladding layers for a III-N UV laser structure. This would alleviate strain and dislocation formation in the structure, and also mitigate the polarization charge. However, a gallium auto-doping mechanism was encountered which prevents the growth of pure ternary InAlN, resulting instead in quaternary InAlGaN. This phenomenon is quantitatively examined and its source is explored.

Identiferoai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/49032
Date20 September 2013
CreatorsLochner, Zachary M.
ContributorsDupuis, Russell D.
PublisherGeorgia Institute of Technology
Source SetsGeorgia Tech Electronic Thesis and Dissertation Archive
Languageen_US
Detected LanguageEnglish
TypeDissertation
Formatapplication/pdf

Page generated in 0.0017 seconds