Three-dimensional macroporous structures (‘opals’ and ‘inverse opals’) can be produced by colloidal crystal templating, one of the most intensively studied areas in materials science today. There are several potential advantages of lithium-ion battery electrodes based on inverse opal structures. High electrode surface, easier electrolyte access to the bulk of electrode and reduced lithium diffusion lengths allow higher discharge rates. Highly open structures provide for better mechanical stability to volume swings during cycling.
Silicon is one of the most promising anode materials for lithium-ion batteries. Its theoretical capacity exceeds capacities of all other materials besides metallic lithium. Silicon is abundant, cheap, and its use would allow for incorporation of microbattery production into the semiconductor manufacturing. Performance of silicon is restricted mainly by large volume changes during cycling.
The objective of this work was to investigate how the inverse opal structures influence the performance of silicon electrodes. Several types of silicon-based inverse opal films were synthesised, and their electrochemical performance was studied.
Amorphous silicon inverse opals were fabricated via chemical vapour deposition and characterised by various techniques. Galvanostatic cycling of these materials confirmed the feasibility of the approach taken, since the electrodes demonstrated high capacities and decent capacity retentions. The rate performance of amorphous silicon inverse opals was unsatisfactory due to low conductivity of silicon. The conductivity of silicon inverse opals was improved by crystallisation. Nanocrystalline silicon inverse opals demonstrated much better rate capabilities, but the capacities faded to zero after several cycles.
Silicon-carbon composite inverse opal materials were synthesised by depositing a thin layer of carbon via pyrolysis of a sucrose-based precursor onto the silicon inverse opals in an attempt to further increase conductivity and achieve mechanical stabilisation of the structures. The amount of carbon deposited proved to be insufficient to stabilise the structures, and silicon-carbon composites demonstrated unsatisfactory electrochemical behaviour.
Carbon inverse opals were coated with amorphous silicon producing another type of macroporous composites. These electrodes demonstrated significant improvement both in capacity retentions and in rate capabilities. The inner carbon matrix not only increased the material conductivity, but also resulted in lower silicon pulverisation during cycling.
| Identifer | oai:union.ndltd.org:TORONTO/oai:tspace.library.utoronto.ca:1807/16726 |
| Date | 19 January 2009 |
| Creators | Esmanski, Alexei |
| Contributors | Ozin, Geoffrey Alan |
| Source Sets | University of Toronto |
| Language | en_ca |
| Detected Language | English |
| Type | Thesis |
| Format | 33229819 bytes, application/pdf |