Previous issue date: 2008 / Resumo: Este trabalho teve co:mo objetivo avaliar a tixoconformabilidade de ligas Al-Xwt%Si2,5wt%Cu-0,5wt%Mg, abrangendo desde a obtenção das ligas tixofundidas até sua completa caracterização em termos de macro e microestrutura e comportamento viscoso. Ligas Al-1,Owt%Si-2,5wt%Cu-0,5wt%Mg, Al-2,Owt%Si-2,5wt%Cu-0,5wt%Mg, Al-4,Owt%Si2,5wt%Cu-0,5wt%Mg e Al-7,Owt%Si-2,5wt%Cu-0,5wt%Mg foram produzidas via ultra-refino de grãos utilizando o refinador Al-5,Owt%Ti-l,Owt%B. Os materiais foram submetidos a tratamentos térmicos de reaquecimento pelos.tempos de Os, 30s, 90s e 21Os, para duas condições de frações sólidas, 45% e 60%. As ligas contendo 1,Owt%Si, 2,Owt%Si e 4,Owt%Si mostraram-se. bastante próximas em termos de viscosidade aparente, no entanto, a liga com 4,Owt%Si apresentou melhor desempenho em termos de globularização, expressa pelo RQI. Já a liga contendo 7,Owt%Si mostrou-se dendrítica para todas as condições estudadas, o que dificulta sua aplicação nos processos de tixoconformação Os tempos de tratamento térmico agem no sentido de promover a globularização das partículas de fase primária, de forma que os melhores resultados de viscosidade foram alcançados para ligas submetidas aos tempos de 21 Os. As frações sólidas de 45% e 60% não apresentaram diferenças significativas em termos de RQI, porém as ligas contendo menor fração sólida apresentaram melhor desempenho em termos de viscosidade aparente, da ordem de 105Pa.s / Abstract: The goal of this work was to evaluate the thixoformability of Al-Xwt%Si-2.5wt%CuO.5wt%Mg alIoys, including the thixocasting of all alloys and their complete characterization in terms of macro and microstructures and rheological behavior. Al-l.0wt%Si-2.5wt%CuO.5wt%Mg, Al-2.0wt%Si-2.5wt%Cu-0.5wt%Mg, Al-4.0wt%Si-2.5wt%Cu-0.5wt%Mg and Al-7.0wt%Si-2.5wt%Cu-0.5wt%Mg alloys were produced by ultra-refining by addiction of Al5.0wt%Ti-1.0wt%B master alIoy. The materials were submitted to re-heating treatment for Os, 30s, 90s and 2l0s in two conditions, 45% al!d 60% of solid fraction. 1.0wt%Si, 2.0wt%Si and 4.0wt%Si alloys showed very similar results for apparent viscosity, however the 4.0wt%Si alloy showed better performance in terms of globularization, measured by RQI. Thixocast 7.0wt%Si alloy presented dendrictic structures for alI conditions analyzed, making its application too difficult for thixoforming processes. Re-heating treatment times promote the solid phase particles globularization, so that the alloys treated during 210s achieved better results for apparent viscosity. Both 45% and 60% solid fractions did not show significant differences in terms of RQI, but the alloys containing lower solid fraction showed better performance for apparent viscosity, in the order of 105Pa.s / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/264018 |
| Date | 28 July 2008 |
| Creators | Benati, Davi Munhoz, 1981- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Zoqui, Eugênio José, 1965-, Robert, Maria Helena, Fogagnolo, João Batista |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 133p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0074 seconds