Avaliação da tixoconformabilidade das ligas AA 2011 e AA 2014 / Avaliation of the thixoconformability of AA 2011 and AA 2014 alloys

Orientador: Eugênio José Zoqui / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-16T15:58:35Z (GMT). No. of bitstreams: 1
Proni_CeciliaTerezaWeishaupt_M.pdf: 17001263 bytes, checksum: 25c148a2e84c82f917de77b96b714fb6 (MD5)
Previous issue date: 2010 / Resumo: A tixoconformação é uma técnica de processamento de materiais no estado semi-sólido que permite a produção de peças com geometrias near net shape com melhores propriedades mecânicas e com razoável redução no custo final de produção, se comparados aos métodos de fundição e conformação plástica tradicionais. Dentro das várias possibilidades de materiais passíveis de trabalho por esta via, as ligas de alumínio são as mais utilizadas, servindo a diversos segmentos industriais. Contudo, o fornecimento de matéria prima próprias ao tixo-processamento está restrito a alguns produtores, justificando a necessidade de aprofundamento e ampliação de conhecimento com respeito às ligas já produzidas por fundição convencional. Este trabalho apresenta um exame da viabilidade de tixoconformação de duas ligas comerciais: AA 2011 e AA 2014. Esta avaliação foi executada em três etapas distintas: 1) análise dos seus constituintes, das temperaturas de fusão e de solidificação, dos microprecipitados existentes e dos tipos de porosidade; 2) reaquecimento de amostras para observar a resposta à globularização em duas temperaturas distintas (duas frações sólidas) e em quatro tempos de espera diferentes, com a posterior análise quantitativa por meio da metalografia; 3) ensaios de viscosidade nas mesmas condições, com posterior análise microestrutural via MEV e EDS das amostras que apresentaram valores de viscosidade muito altos. Os resultados destas avaliações mostraram que estas duas ligas são tixoconformáveis até a temperatura de 610°C, pois apresentaram valores de viscosidade abaixo de 1x106 Pa.s e tensão máxima abaixo de conformação de 1,0 MPa, conforme escolhas adequadas entre tempos de espera e taxa de aquecimento. Porém, também foi constatada a formação de alumina nos poros de algumas amostras após o reaquecimento necessário à tixoconformação, fornecendo um valor mais alto de viscosidade para estas amostras, se em comparação aos valores encontrados em outros ensaios com pouca ou nenhuma formação de alumina. A eliminação de porosidade na matéria prima com a conseqüente minimização do surgimento de alumina viabilizará a tixoconformação de ambas as ligas / Abstract: Thixoforming is a technique for processing materials in the semi-solid state which allows the production of parts near-net-shape geometries, with better mechanical properties and reasonable reduction in the final production cost, compared to traditional casting and plastic forming. Among the various possibilities of materials that can work in this way, aluminium alloys are the most used. However, the world provision of raw material for thixoforming is restricted to few producers, justifying the need for deepening and widening of knowledge with respect to alloys already produced by the conventional casting industries. This dissertation presents an examination of the feasibility of thixoforming of two commercial alloys: AA 2011 and AA 2014. This evaluation was performed in three steps: 1) analysis of their constituents, analysis of melting and solidification temperatures, analysis of the existing micro precipitates and quantity and types of porosity, 2) reheating samples to observe the globularization response to two different temperatures (two solid fractions) and four holding times, with the subsequent quantitative analysis by metallography, 3) tests of the viscosity under the same conditions, with subsequent microstructural analysis by SEM and EDS of the samples that showed very high viscosity values. The results of these evaluations showed that these two alloys are thixoformable up to temperatures of 610°C, since their viscosity values were achieved below than 106 Pa.s, and consequently maximum conformation stress of 1.0 MPa, as appropriate choices between waiting times and heating rate were achieved. However, the formation of alumina in the pores of some samples after the necessary reheating to previous to thixoforming, provide a higher value of viscosity, when compared to values found in other trials with little or no alumina. The elimination of porosity in the raw material, with the consequent minimizing the appearance of alumina will make possible the thixoforming of both alloys / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/264031
Date07 January 2010
CreatorsProni, Cecilia Tereza Weishaupt, 1959-
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Zoqui, Eugênio José, 1965-, Fogagnolo, João Batista, Goldenstein, Helio
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format130 p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0029 seconds