Análise da influência dos solutos Zr e Ti sobre as propriedades mecânica, elétrica e de termorresistência de uma liga Al-Cu-Fe-Si destinada a Tx e a Dx de energia elétrica

Submitted by Cleide Dantas (cleidedantas@ufpa.br) on 2014-04-07T15:03:11Z
No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_AnaliseInfluenciaSolutos.pdf: 4870883 bytes, checksum: d7109b6377ff94f74d47309e592e6d8e (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2014-06-16T16:25:19Z (GMT) No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_AnaliseInfluenciaSolutos.pdf: 4870883 bytes, checksum: d7109b6377ff94f74d47309e592e6d8e (MD5) / Made available in DSpace on 2014-06-16T16:25:19Z (GMT). No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_AnaliseInfluenciaSolutos.pdf: 4870883 bytes, checksum: d7109b6377ff94f74d47309e592e6d8e (MD5)
Previous issue date: 2012 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / CNPq - Conselho Nacional de Desenvolvimento Científico e Tecnológico / Eletronorte - Centrais Elétricas do Norte do Brasil S/A / O contexto energético mundial apresenta um aumento constante do consumo de energia elétrica no último século, desta forma exigindo a pesquisa de novos materiais para a aplicação em cabos e fios condutores de eletricidade. A partir destas demandas por novos materiais, desenvolveu-se uma análise da influência dos solutos zircônio e titânio na modificação de características importantes de uma liga Al-Cu-Fe-Si, destinada a ser o meio condutor de energia elétrica, almejando obter propriedades termorresistentes. Para a
realização deste estudo, as ligas foram obtidas por fundição direta em lingoteira metálica em formato “U”, a partir do Al-EC, fixando-se na liga-base os teores de 0,05% Cu, [0,24 a 0,28]% Fe e 0,7% de Si, e em seguida, inserindo-se os teores de 0,26% Zr e 0,26% Ti. O
experimento foi dividido em duas etapas, ETAPA A e ETAPA B, respectivamente, com o intuito de se avaliar as características mecânicas, elétricas e estruturais das ligas. Os corpos de
prova após laminação a frio (nos diâmetros 2,7; 3,0; 3,8 e 4,0 mm) foram analisados sem tratamento térmico (STT) e com tratamento térmico (CTT): 230 ºC por uma hora, de acordo com o protocolo COPEL, 310 ºC e 390 ºC por uma hora, visando avaliar a ermorresistência em temperaturas mais elevadas, a estabilidade térmica e analisar as microestruturas desenvolvidas em tais tratamentos térmicos (TT). Verificou-se que o Ti tem maior capacidade de refinar o grão em relação ao Zr, que apresenta grãos menos refinados, porém com melhores propriedades físicas e apresentando-se termorresistente. / The global energy context presents a steady increase in electricity consumption in the
last century, thus requiring the search for new materials for use in wire and cable conductors
of electricity. From these demands for new materials, was developed an analysis of the
influence of solute titanium and zirconium in the modification of important characteristics of
the Al-Cu-Fe-Si alloy, destined to be the middle conductor of electricity, aiming to get
properties resistant to heat. For this study, the alloys were obtained by direct casting in Ushaped
metal ingots, from the Al-EC, standing at the base levels of 0.05 wt% Cu, [0.24 to
0.28] wt% Fe and 0.7 wt% Si, and then inserting the contents of 0.26 wt% Zr and 0.26 wt%
Ti. The experiments were, divided in two steps, STEP A and STEP B , respectively. In order
to characterize mechanical, electrical and structure of alloys. The specimens after cold rolling
(in diameters of 2.7, 3.0, 3.8 and 4.0 mm) were analyzed without heat treatment (STT) and
with heat treatment (CTT): 230 °C for one hour, according to the protocol COPEL
(Companhia Paranaense de Energia Elétrica), 310 °C and 390 °C for one hour, to evaluate the
heat resistance at higher temperatures, thermal stability and analyze the microstructures
developed in these heat treatments (TT). It was found that Ti has more capacity to refine the
grain compared to Zr, which has less refined grains, but with better physical properties are
presented and heat resistant.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/5073
Date10 January 2012
CreatorsMACHADO, Paulo Cordeiro
ContributorsQUARESMA, José Maria do Vale
PublisherUniversidade Federal do Pará, Programa de Pós-Graduação em Engenharia Mecânica, UFPA, Brasil, Instituto de Tecnologia
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0021 seconds